Abstract:The interface morphology of the bonding layer has a considerable effect on the damage and failure of sandwich-structured thermal barrier coatings. This work investigated the comprehensive effects of a grooved texture produced using laser ablation on the local surface strain, interfacial stress and strain, and crack behavior of the bonding layer in a thermal barrier coating system. The distribution and evolution of the local surface strain was obtained using the digital image correlation method. The interfacial stress, and the strain between the ceramic and bonding layers, were determined through a simulation of the plane-strain model, and the morphology and propagation of cracks were observed in thermal barrier coatings under an external tensile load. The results indicated that the local surface strain of the thermal barrier coating increased with the texturization of the bonding layer, whereas the fluctuation decreased. There were two inflection points in the local surface strain–time curves, corresponding to the initiation of surface cracks and that of interfacial transverse cracks. The surface cracks were initiated earlier than those without the texturization of the bonding layer. However, the behavior of the interfacial cracks was more complicated. If the roughness of the texture, defined as Rc, was small, the surface cracks propagated vertically to the interface between the ceramic and bonding layers, and turned into transverse cracks, leading to a separation of the ceramic layer. If Rc was greater than 22 μm, the surface cracks went further down to the interface between the bonding layer and substrate, and propagated horizontally, resulting in the separation of both the ceramic and bonding layers. Meanwhile, interfacial cracking and separation were deferred. A large roughness resulted in good cohesion between the ceramic and bonding layers, and a high stiffness for the coating, which improved the damage resistance and extended the life of the coating.

Cracking Behavior and Delamination Mechanism of Lamellar Structured TBC with Localized Mixed Oxides

Activating Continuous Dislocation Pinning Enhanced Toughness of Nanocomposite Coating Through Specially Oriented Semicoherent Heterointerface Lattice Distortion

Effect of Thermal Growth Oxide Composition and Morphology on Local Stresses in Thermal Barrier Coatings

A Diffusion-Coupled Cohesive Element Model for Cracking Analysis of Thermal Barrier Coatings

Modeling 3D TGO dynamic growth and stresses and the resulting modes of buckling failure in thermal barrier coatings

Failure Mechanism of EB-PVD Thermal Barrier Coatings under the Synergistic Effect of Thermal Shock and CMAS Corrosion

Thermomechanical and Thermal Gradient Mechanical Fatigue Lifetime of Thermal Barrier Coating Systems

On crack evolution with texturization of bonding layer in thermal barrier coating

Comprehensive Understanding of the Effect of TGO Growth Modes on Thermal Barrier Coating Failure Based on a Simulation

Chemo-thermo-mechanical modeling of EB-PVD TBC failure subjected to isothermal and cyclic thermal exposures

Atmospheric plasma sprayed thick thermal barrier coatings: Microstructure, thermal shock behaviors and failure mechanism

Influence of non-uniform feature of thermally grown oxide thickness on the local stress state and cracking behavior in TBC

Microstructure characteristics and deformation-induced crystalline-to-amorphous phase transformation in thermal barrier coatings during thermal cycling

Microcrack Morphology in the Thermal Insulation Performance of 8YSZ Thermal Barrier Coatings: A Mesoscale Numerical Study

Crack Initiation and Propagation Mechanism of Al2O3-DBC Substrate During Thermal Cycling Test

Thermal Cycling Behavior of Thermal Barrier Coatings with MCrAlY Bond Coat Irradiated by High-Current Pulsed Electron Beam

Effect of Interface Curvature on Local Growth Behavior and Stress of Thermal Barrier Coatings

Phase-Field Modeling of Thermally-Grown Oxide and Damage Evolution in Environmental Barrier Coatings

A Simulation Study on the Crack Propagation Behavior of Nanostructured Thermal Barrier Coatings with Tailored Microstructure

Finite Element Analysis of Interface Undulation and Interface Delamination in the MCrAlY Coating System Under Thermal Cycling: Considering Oxide Thickness and Top-Coat Effects

Study on Construction Mechanism of Ceramic–Metal Thermal Barrier Coating System by Plasma Spraying