High Strength and Deformation Stability Achieved in CrCoNi Alloy Containing Deformable Oxides

Jiawei Zou,Xiaoqian Fu,Yajing Song,Tianxin Li,Yiping Lu,Ze Zhang,Qian Yu

DOI: https://doi.org/10.1016/j.jmst.2022.06.026

2023-01-01

Abstract:Hard secondary phases usually strengthen alloys at the expense of ductility.In this work,we made a dual-phase CrCoNi-O alloy containing a face centered cubic matrix and chromium oxide.On one side,the dispersed chromium oxide nano-particles impeded dislocation movement and increased the strength of the alloy.On another side,the spreading lattice distortion in CrCoNi-O high entropy solution locally relieved the severe interfacial mismatch and led to nanoscale variation of interfacial strain at the matrix-oxide interface,which facilitated dislocations'transmission from one phase to another.Consequently,unlike the strong but brittle oxide nanoparticles used before,the oxide phase here can afford signif-icant dislocation activities during material's plastic deformation.Comparing the mechanical properties of CrCoNi-O alloys with and without chromium oxide particles,it was found that the yield strength of the dual-phase samples was twice of the single phase CrCoNi-O alloy and strong strain hardening was obtained with ultra-high deformation stability.High density of nanotwins formed in dual-phase samples under high stress,resulting in significant strain hardening according to the well-known twinning-induced plasticity(TWIP)effect.Our results shed light on optimizing the combination of strength and plasticity of compounds by modulating the variation of interfacial strain field based on the spreading lattice distor-tion.