High strength and ductility in a dual-phase hetero-structured AlCoCrFeNi2.1 eutectic high-entropy alloy by powder metallurgy

Siyuan Peng,Shuai Feng,Zhenfei Jiang,Jie Ren,Shengbiao Zhang,Yanfang Liu,Liang Zhang,Wenyi He,Zhongqiang Liu,Shuai Guan,Zhiyu Xiao,Wen Chen
DOI: https://doi.org/10.1080/21663831.2024.2332608
2024-03-29
Materials Research Letters
Abstract:We used powder hot extrusion followed by annealing to fabricate a dual-phase AlCoCrFeNi 2.1 eutectic high-entropy alloy consisting of both non-recrystallized and recrystallized grains with dense nano-sized precipitates arranged in heterogeneous structures. The resulting alloy exhibits superior tensile properties with a yield strength of ∼1.2 GPa, an ultimate tensile strength of ∼1.5 GPa, and a uniform elongation of ∼18%. Such multiscale microstructure results in exceptional strain hardening of the AlCoCrFeNi 2.1 alloy by activating remarkable hetero-deformation induced (HDI) stresses. Our study provides an effective approach to fabricating high-performance structural materials via dual-phase heterogeneous microstructure design.
materials science, multidisciplinary
What problem does this paper attempt to address?
The problem that this paper attempts to solve is in materials science, especially for materials in structural applications such as transportation, aerospace, and advanced energy systems, how to break the mutually exclusive relationship between strength and ductility (i.e., the strength - ductility trade - off). Specifically, this paper aims to achieve the combination of high strength and high ductility by designing the AlCoCrFeNi 2.1 eutectic high - entropy alloy with a dual - phase heterogeneous microstructure. Through the powder metallurgy method (annealing treatment after hot extrusion), the authors successfully prepared this alloy and observed a significant improvement in mechanical properties, including a yield strength of about 1.2 GPa, a tensile strength of about 1.5 GPa, and a uniform elongation of about 18%. These improvements in properties are mainly attributed to the role of heterogeneous deformation - induced (HDI) stress, which is caused by dislocation tangles and accumulations formed at the FCC and B2 phase interfaces, thus providing a higher strain - hardening capacity.