Ultrasonic provoked network-like intragrain carbide precipitations strengthen and ductilize a C-doped CoCrNi medium entropy alloy

Zu Li,Xiang Long,Siyuan Zhang,Haowei Deng,Meng Zhang,Tao Zhang

DOI: https://doi.org/10.1016/j.scriptamat.2023.115633

IF: 6.302

2023-06-27

Scripta Materialia

Abstract:A strategy bypassing "rolling+annealing" while involving merely ultrasonic vibration-modulated static compressive loading was established to enhance the strength-ductility synergy in a C-doped CoCrNi medium entropy alloy. Specifically, by superimposing ultrasonic vibration of 20 KHz in frequency and 20 μm in amplitude onto a compressive load of ∼180 MPa (∼60% of yield strength) applied on a coarse grain CoCrNiC 0.1 alloy for 25 min, yield strength, ultimate tensile strength, and total elongation of the alloy were largely improved to 530 MPa, 950 MPa, and 36.5%, showing respectively an increment of 77%, 28%, and 53% from the original state (300 MPa, 740 MPa, and 23.8%). Structure analysis on the ultrasonically processed CoCrNiC 0.1 alloy indicates that intragrain precipitation of Cr7C3 networks of a characteristic size ∼20 μm provoked by ultrasonic vibration was the main cause for the strength-ductility synergy. Our work provides a promising path to engineer the strength-ductility synergy in precipitation-strengthened alloys.

materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering