Significantly Toughened PZT-based Piezoelectric Ceramics Simultaneously Keeping Excellent Electrical Properties Via Incorporating Trace Amount of Yttria-Partially-stabilized Zirconia

Zhidong Zhang,Bin Yang,Wei Gu,Haiyan Yu,Letao Yang,Xunzhong Shang,Taosheng Zhou,Jinming Guo

DOI: https://doi.org/10.1016/j.ceramint.2022.08.299

IF: 5.532

2022-01-01

Ceramics International

Abstract:Piezoelectric ceramics are prone to cracking during functioning due to the repetitively applied high stress. Hence, toughened ceramics with robust microstructures are highly desired for resisting the potential cracks. Toughening of Lead Zirconium Titanate (PZT) based piezoelectric ceramics with high d(33).g(33) for ignition applications is investigated in this work. Yttria-partially-stabilized zirconia (YPSZ) particles were incorporated into the PZT-based piezoelectric ceramics via conventional solid state reaction. Measurements of mechanical properties of as-sintered ceramics indicate that incorporation of an appropriate amount of YPSZ significantly improves the fracture toughness of PZT-based ceramics by 38.7%, meanwhile the piezoelectric coefficient still remains at a high level with a decrease of less than 7%. When doping 0.5 wt% YPSZ, the optimal comprehensive properties can be obtained as follows: fracture toughness K-IC = 1.41 MPa.m(1/2), Vickers hardness H-V = 4.60 GPa, piezoelectric coefficient d(33) = 462 pC/N, planar electromechanical coupling factor k(p) = 60.1%, and dielectric constant epsilon(T)(33)/epsilon(0) = 1750. This successful toughening mechanism paves a way in developing functional ceramics simultaneously possessing superior fracture toughness and electrical properties via doping an appropriate content of YPSZ submicron particles.