Synergistic Effects of Fe and C on Microstructure and Properties of Nb-Ti-Si Based Alloys

Qibin Wang,Qi Wang,Ruirun Chen,Xiaowei Wang,Yanqing Su,Hengzhi Fu
DOI: https://doi.org/10.1016/j.jallcom.2022.168167
2022-01-01
SSRN Electronic Journal
Abstract:Nb-silicide in situ composites have been considered as alternatives applied for nickel-based superalloys in aerospace field. The synergistic effects of Fe and C on microstructural evolution, properties and hot deformation behavior of Nb-24Ti-16Si-2Al-3 V-xFe-yC alloys are investigated. Results show that the microstructure of 4Fe-1 C alloy consists of Nbss/β-(Nb, X)5Si3 eutectics and γ-(Nb, X)5Si3 blocks, while the TiC particles precipitate with the increase of C content. For 6Fe-yC alloys, a new silicide phase Nb4FeSi is formed around the (Nb, X)5Si3 phase. Element Fe is mainly distributed in Nb4FeSi and part of Fe-rich (Nb, X)5Si3, while C is mainly dissolved in TiC particles, followed by Nbss. The orientation relationship of Nbss and TiC in accordance with {110}Nbss//{111}TiC. The room temperature fracture toughness and compressive strength exhibit a trend of enhancing first and then reducing with the co-addition of Fe and C. The KQ value of the 4Fe-3 C alloy reaches the highest with a mean of 14.49 MPa·m1/2. Element C can effectively promote the high temperature compressive strength, and Fe can improve the hot deformability. The initial eutectic coupled structure has evolved into a continuous Nbss matrix with dispersed silicides during hot deformation. Furthermore, the splitting mechanism of silicides during hot deformation is determined.
What problem does this paper attempt to address?