Synchronous Enhancement of Hot Deformation Capacity and Properties of Nb-Ti-Si Based Alloys by Composite Alloying of Fe and V

Qibin Wang,Qi Wang,Ruirun Chen,Xiaowei Wang,Hengzhi Fu,Yanqing Su

DOI: https://doi.org/10.2139/ssrn.4191463

2022-01-01

SSRN Electronic Journal

Abstract:To improve the thermal deformation ability of Nb-Si alloy whilst increasing the comprehension properties, the synergistic effects of Fe and V on microstructural evolution and properties of Nb-24Ti-16Si-2Al alloys are investigated. Results show that with the co-addition of Fe and V, the formation of (Nb, X) 3 Si is suppressed and a new silicide Nb 4 FeSi is obtained. The constituent phases of the alloys transform from Nbss + β-(Nb, X) 5 Si 3 + (Nb, X) 3 Si to Nbss + β-(Nb, X) 5 Si 3 + Nb 4 FeSi. Element Fe is primarily enriched in Nb 4 FeSi phase, while V is mainly dissolved in Nbss and Nb 4 FeSi phases. The room temperature fracture toughness is significantly enhanced by the co-addition of Fe and V, in which the K Q value of 2Fe-5V alloy is reached to 12.87 MPa·m 1/2 , improved by 96.2 % compared with the initial alloy. Hot deformation behavior is sensitive to composition and temperature, and an excellent hot deformation ability is exhibited as close to the melting point of Nb 4 FeSi (1348 ℃). After hot deformation, the composition homogenization is achieved and the Nbss/β-(Nb, X) 5 Si 3 eutectics have evolved into a continuous Nbss matrix with dispersed β-(Nb, X) 5 Si 3 particles. The Fe enrichment region will become the source of the splitting of (Nb, X) 5 Si 3 during hot deformation, resulting in the fragmentation and refinement of the coarse silicides.