Excellent energy storage performance in NaNbO 3 -based relaxor antiferroeic ceramics under a low electric field

Xuxin Cheng,Xiaoming Chen,Pengyuan Fan

DOI: https://doi.org/10.1007/s10832-022-00283-w

2022-01-01

Journal of Electroceramics

Abstract:NaNbO 3 -based antiferroelectric (AFE) ceramics have the prominent advantages of stable performance and low cost. However, its energy storage property is often remarkably limited by the hysteresis of the antiferroelectric to ferroelectric phase transformation. In this work, 0.88Na(Nb 1− x Ta x )O 3 –0.12Bi 0.2 Sr 0.7 TiO 3 ( x = 0–0.075) antiferroelectric ceramics were synthesized using a conventional mixed oxide route. Ta 5+ were completely dissolved into the lattice of 0.88NaNbO 3 –0.12Bi 0.2 Sr 0.7 TiO 3 to form a pure perovskite structure. With increased Ta content, the AFE orthogonal P phase was replaced by AFE orthogonal R phase progressively. Meanwhile, the dielectric constant curve showed relaxor-like properties. As a result, slender P–E curves with reduced hysteresis loss and decreased residual polarization were achieved. Interestingly, a large recoverable energy storage density ( W rec ~ 2.16 J cm −3 ) and high energy storage efficiency ( η ~ 80.7%) were obtained simultaneously under a low driving electric field of 15 kV mm −1 at doping ratio ( x ) of 0.075. In addition, the 0.88Na(Nb 0.925 Ta 0.075 )O 3 –0.12Bi 0.2 Sr 0.7 TiO 3 sample exhibited excellent temperature stability, indicating an ideal candidate in future pulsed power capacitor.