High Energy Storage Density in NaNbO3 Antiferroelectrics with Double Hysteresis Loop

Li Ma,Zhenpei Chen,Gengguang Luo,Zhiyi Che,Chao Xu,Dongliang Shan,Zhenyong Cen,Qin Feng,Xiyong Chen,Toyohisa Fujita,Ye Zhu,Yunya Liu,Jing-Feng Li,Shujun Zhang,Nengneng Luo

DOI: https://doi.org/10.1016/j.jmat.2023.11.003

IF: 8.589

2024-01-01

Journal of Materiomics

Abstract:Antiferroelectrics (AFEs) possess great potential for high performance dielectric capacitors, due to their distinct double hysteresis loop with high maximum polarization and low remnant polarization. However, the well-known NaNbO3 lead-free antiferroelectric (AFE) ceramic usually exhibits square-like P-E loop related to the irreversible AFE P phase to ferroelectric (FE) Q phase transition, yielding low recoverable energy storage density (Wrec). Herein, significantly improved Wrec up to 3.3 J/cm3 with good energy storage efficiency (h) of 42.4% was achieved in Na0.7Ag0.3Nb0.7Ta0.3O3 (30Ag-30Ta) ceramic with welldefined double P-E loop, by tailoring the A-site electronegativity with Ag & thorn; and B-site polarizability with Ta5 & thorn;. The Transmission Electron Microscope, Piezoresponse Force Microscope and in-situ Raman spectra results verified a good reversibility between AFE P phase and high-field-induced FE Q phase. The improved stability of AFE P phase, being responsible for the double P-E loop and improved Wrec, was attributed to the decreased octahedral tilting angles and cation displacements. This mechanism was revealed by synchrotron X-ray diffraction and Scanning Transmission Electron microscope. This work provides a good paradigm for achieving double P-E loop and high energy storage density in NaNbO3based ceramics. (c) 2023 The Authors. Published by Elsevier B.V. on behalf of The Chinese Ceramic Society. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).