High Energy Density in Ag 0.5 Na 0.5 (nb 1-X Ta X )O 3 Antiferroelectric Ceramics

Ye Tian,Lei Li,Yonghao Xu,Ming Ma,Chen,Zixiong Sun,Liaona She,Guanjun Chen,Tong Wang,Wanyin Ge,Xiaoyong Wei,Li Jin

DOI: https://doi.org/10.1016/j.jeurceramsoc.2024.04.049

IF: 5.7

2024-01-01

Journal of the European Ceramic Society

Abstract:There has been significant interest in AgNbO 3 -based antiferroelectric ceramics, recently, due to their ability to achieve high energy storage density ( W rec ). However, fabricating their commercial products faces challenges due to chemically unstable and expensive Ag 2 O. To reduce Ag 2 O contents, we fabricated (Ag 0.5 Na 0.5 )(Nb 1- x Ta x )O 3 (ANNT100 x ) ceramics. The results reveal that Ta-substitution plays a dual role: inducing chemical pressure to compress the unit cell along spontaneous polarization direction, enhancing antiferroelectric stability; and increasing the band gap ( E g ), boosting intrinsic breakdown strength ( E b ). These crucial factors contribute to the enhanced W rec achieved in ANNT50. Notably, ANNT50 ceramics fabricated by the rolling process exhibit higher E b ( =578 kV/cm) than the conventional process, favoring the complete triggering of " double " polarization with significantly enhanced W rec ( = 6.5 J/cm 3 ). Discharge results indicate that the ceramic displays high power density ( P avg = 78 MW/cm 3 ) and discharge energy ( W dis = 5.86 J/cm 3 ), which can rival currently reported Ag (Nb, Ta)O 3 ceramics.