Interface Feature via Key Factor on Adhesion of CrN Multilayer and Alloy Substrate
Shuai Xu,Zhuo Zhao,Yanwen Zhou,Dongxu Chen,Kaice Zhang,Tong Li,Yangtao Zhou,Aihuai Wang
DOI: https://doi.org/10.1016/j.apsusc.2023.157492
IF: 6.7
2023-05-13
Applied Surface Science
Abstract:CrN multilayer coatings were deposited on 316L stainless steel, which has a high modulus, and TC4 titanium alloy, which exhibits the opposite properties, to reveal adhesion mechanisms and deformation behavior of the coating/substrate systems. Because of the different microstructures, the coatings' morphologies varied from single polygon on the 316L to polygon and rectangle-mixed shapes on the TC4. On 316L, the cracks initiated from the Cr/CrN interfaces and propagated into the CrN layer, which stopped within it. On TC4, the cracks propagated through the CrN layer. The coherent nanocrystal interfaces in CrN/Cr/316L exhibited orderly bending, revealing the presence of strong interfacial bonds. The undeformed interfaces in CrN/Cr/TC4 indicated incompatible deformation and weak bonds. This was consistent with the fact that on TC4, the Cr/CrN interface tensile stress was high, at 123.1 GPa, while it was lower on 316L, at 99.3 GPa. The W p /W e ratio of CrN/TC4, namely 1.94, was lower than that of CrN/316L, namely 2.61. This indicated that CrN/316L had a high energy-absorption ability because of compatible plastic deformation. The failure mechanism observed between the coating/TC4 was attributed to the differences in their moduli, which led to incompatible deformation, high interfacial tensile stress, and low absorption capability for external work.
chemistry, physical,physics, applied, condensed matter,materials science, coatings & films