Microstructure and Mechanical Properties of a CrCN/Cr Multilayer Film

Eryong Liu,Bo Yu,Yuan Xue,Jibin Pu,Shuangming Du,Huiling Du
DOI: https://doi.org/10.1088/2053-1591/abb4f8
IF: 2.025
2020-01-01
Materials Research Express
Abstract:CrCN/Cr multilayer films were synthesized by multi-arc ion plating deposition technique, and the microstructure, mechanical and tribological properties of films were systematically investigated. The results showed that the thickness of the CrCN and Cr layers in CrCN/Cr multilayer films was between 2.1 mu m to 0.45 mu m and 90 nm, respectively. X-Ray diffraction results indicated that the composite films were composed of CrN, Cr(7)C(3)and metallic Cr phase, then the mechanical and tribological properties results confirmed that the multilayer structure not only increased the hardness and toughness of the CrCN multilayer film but also decreased the friction coefficient (16%) and wear rate (45%) when compared with a CrN film. This result was attributed to the presence of a complete and dense lubricating film on the worn surface. Therefore, the excellent performance of the CrCN/Cr multilayer films supports their potential application as a replacement for CrN films in industrial applications.
What problem does this paper attempt to address?