Tensile mechanism of wear-resistant Cr/CrN/Cr/CrAlN multilayer film
Di Wang,Tian Tian,Song-sheng Lin,Nan Zhao,Han Liu,Jun-hui Liu,Yu Wang,Lei Li,Hai-yan Li,Qian Shi,Ming-jiang Dai
DOI: https://doi.org/10.1016/j.vacuum.2022.111405
IF: 4
2023-01-01
Vacuum
Abstract:In this work, we deposited the Cr/CrN/Cr/CrAlN multilayer films with various thickness on TC4 titanium alloy substrates by cathodic arc system. The effects of film thickness on microstructure, mechanical properties, tribological properties and tensile properties were mainly investigated. The results show that the thickness of the multilayer film is about 200 nm per cycle for 18, 36, 54 and 72 cycles, and that the number of large particles on the surface increases from 8% to about 13% with increasing film thickness. The residual stress also increased gradually from −1.633 ± 0.082 GPa at 18 cycles to −3.851 ± 0.169 GPa at 72 cycles. And the difference in hardness was not significant, but the best bonding and crack extension resistance was achieved at 54 cycles. The wear resistance of the four groups of multilayer films was good, with a coefficient of friction of around 0.6. In addition, the tensile strength of the coated samples increased compared to the uncoated samples, with an increase of nearly 3% in the strength index, and the phenomenon of increasing and then decreasing with the number of film cycles, but with a decreasing trend in elongation after break. Based on this phenomenon, the fracture mechanism of the hard film affecting the titanium alloy substrate was analysed.
materials science, multidisciplinary,physics, applied