Abstract:Ti-6.5Al-2Zr-1Mo-1V/TiB metal matrix composites with 3 wt.% of TiB2 were obtained using vacuum arc melting and spark plasma sintering methods and compared with an unreinforced Ti-6.5Al-2Zr-1Mo-1V alloy. The microstructures of the unreinforced Ti6.5Al-2Zr-1Mo-1V alloy in the as-cast and as-sintered conditions were quite typical and consisted of colonies of α-lamellae embedded in the β matrix. The microstructure of the as-cast Ti-6.5Al-2Zr-1Mo-1V/TiB composite composed of TiB fibers randomly distributed within the two-phase α/β matrix, while the as-sintered composite had a network-like microstructure, in which areas of the two-phase α/β matrix were delineated by walls of TiB fibers. At room temperature, the yield strength of the as-cast and as-sintered Ti-6.5Al-2Zr-1Mo-1V alloy were 800 and 915 MPa, respectively, with a plasticity of 18% in both conditions. The addition of TiB fibers contributed to a ~40 and 50% strength increment, with values of 1100 and 1370 MPa for the as-cast and as-sintered composites, respectively. In the as-sintered composite, the strengthening effect reduced at 400 °C and almost disappeared at elevated temperatures of 800–950 °C. The as-cast composite showed much higher strength during warm and hot deformation—at 800–950 °C, the yield strength of the as-cast composite was 50% higher compared to the Ti-6.5Al-2Zr-1Mo-1V unreinforced alloy. A higher rate and degree of globularization were established for the as-cast composite compared to the unreinforced alloy. For the as-sintered composite, a noticeably lower rate and degree of globularization was shown. During hot compression of the as-cast composite, TiB fibers reoriented towards the metal flow direction, while the network microstructure formed in the as-sintered composite transformed into clusters of borides unevenly distributed within the matrix. Based on the obtained results, the apparent activation energy of plastic deformation was calculated, and the operating deformation mechanisms were discussed both for the as-cast and as-sintered composites. The Arrhenius flow stress model and the dynamic material model were used to evaluate the deformation behavior of composites beyond the experimentally studied temperatures and strain rates.

Comparative Study of Microstructure and Characteristics of Ti6Al4V/TiB Composites Manufactured with Various Powder Metallurgy Approaches

In Situ Ti6Al4V/TiB Composites Prepared by Hydrogen-Assisted Sintering of Blends Containing TiH2 and Ball-Milled Ti+TiB2 Powders

Nearly dense Ti–6Al–4V/TiB composites manufactured via hydrogen assisted BEPM

Microstructure Evolution and Mechanical Behavior of TiB-Reinforced Ti-6.5Al-2Zr-1Mo-1V Matrix Composites Obtained by Vacuum Arc Melting and Spark Plasma Sintering

Microstructure and Mechanical Properties of In Situ TiB2/2024 Composites Fabricated by Powder Metallurgy

Microstructure and Mechanical Properties of Ti-TiH2 Based Matrix Composites Reinforced with xTiB2 Particles Processed by Powder Metallurgy

Microstructures and tensile properties of low-cost TiBw/Ti–6Al–4V composites by vacuum reactive hot pressing

Microstructure and mechanical properties of (TiB+TiC)/Ti composites fabricated in situ via selective laser melting of Ti and B4C powders

Sintering Behavior and Mechanical Properties of Ti–TiBw Composites Prepared with Pre‐alloyed Ti–TiBw Composite Powders

MICROSTRUCTURE AND MECHANICAL PROPERTIES OF IN-SITU SYNTHESIZED TITANIUM MATRIX COMPOSITES PREPARED BY POWDER METALLURGY

Microstructure, densification and mechanical properties of in situ TiBw/Ti2AlNb composites fabricated by spark plasma sintering

Microstructure and Mechanical Properties of In Situ Synthesized Metastable β Titanium Alloy Composite from Low-Cost Elemental Powders

The Effect of Micron-Sized TiB2 Particles on the Properties of Al6061 Strengthened with 4% TiB2 Nano-TiB2

Ballistic performance of titanium-based layered composites made using blended elemental powder metallurgy and hot isostatic pressing

Microstructure of In-Situ Synthesized (tib+tic)/ti Composites Prepared by Hot-pressing

Microstructure and mechanical properties of powder metallurgy Ti-TiBw-xFe titanium matrix composites using Ti-TiBw composite powder

Microstructure and mechanical properties of an in-situ TiB2 particle reinforced AlSi10Mg composite additive manufactured by selective electron beam melting

Microstructure and Mechanical Properties of Cu Matrix Composites Reinforced by TiB2/TiN Ceramic Reinforcements

Microstructural characterization and mechanical properties of (TiC+TiB)/TA15 composites prepared by an in-situ synthesis method

Microstructure and Mechanical Properties of TiB2-Al2O3 Composites

Thermomechanical Processing of a Near-α Ti Matrix Composite Reinforced by TiBw