Abstract:Ti-6.5Al-2Zr-1Mo-1V/TiB metal matrix composites with 3 wt.% of TiB2 were obtained using vacuum arc melting and spark plasma sintering methods and compared with an unreinforced Ti-6.5Al-2Zr-1Mo-1V alloy. The microstructures of the unreinforced Ti6.5Al-2Zr-1Mo-1V alloy in the as-cast and as-sintered conditions were quite typical and consisted of colonies of α-lamellae embedded in the β matrix. The microstructure of the as-cast Ti-6.5Al-2Zr-1Mo-1V/TiB composite composed of TiB fibers randomly distributed within the two-phase α/β matrix, while the as-sintered composite had a network-like microstructure, in which areas of the two-phase α/β matrix were delineated by walls of TiB fibers. At room temperature, the yield strength of the as-cast and as-sintered Ti-6.5Al-2Zr-1Mo-1V alloy were 800 and 915 MPa, respectively, with a plasticity of 18% in both conditions. The addition of TiB fibers contributed to a ~40 and 50% strength increment, with values of 1100 and 1370 MPa for the as-cast and as-sintered composites, respectively. In the as-sintered composite, the strengthening effect reduced at 400 °C and almost disappeared at elevated temperatures of 800–950 °C. The as-cast composite showed much higher strength during warm and hot deformation—at 800–950 °C, the yield strength of the as-cast composite was 50% higher compared to the Ti-6.5Al-2Zr-1Mo-1V unreinforced alloy. A higher rate and degree of globularization were established for the as-cast composite compared to the unreinforced alloy. For the as-sintered composite, a noticeably lower rate and degree of globularization was shown. During hot compression of the as-cast composite, TiB fibers reoriented towards the metal flow direction, while the network microstructure formed in the as-sintered composite transformed into clusters of borides unevenly distributed within the matrix. Based on the obtained results, the apparent activation energy of plastic deformation was calculated, and the operating deformation mechanisms were discussed both for the as-cast and as-sintered composites. The Arrhenius flow stress model and the dynamic material model were used to evaluate the deformation behavior of composites beyond the experimentally studied temperatures and strain rates.

In Situ Ti6Al4V/TiB Composites Prepared by Hydrogen-Assisted Sintering of Blends Containing TiH2 and Ball-Milled Ti+TiB2 Powders

Nearly dense Ti–6Al–4V/TiB composites manufactured via hydrogen assisted BEPM

In Situ TiBw/Ti–6Al–4V Composites with Novel Reinforcement Architecture Fabricated by Reaction Hot Pressing

In situ (TiBw+TiCp)/Ti6Al4V composites with a network reinforcement distribution

Fabrication of an In-Situ Ti-2.6vol%Tic Metal Matrix Composite by Thermomechanical Consolidation of A Tih2-1vol%Cnts Powder Blend

In-situ synthesized TiC/Ti-6Al-4V composites by elemental powder mixing and spark plasma sintering: Microstructural evolution and mechanical properties

Microstructure and Mechanical Properties of in Situ Synthesised (Tic+tib)/ti-6Al-4v Composites Prepared by Powder Metallurgy

Microstructure and mechanical properties of (TiB+TiC)/Ti composites fabricated in situ via selective laser melting of Ti and B4C powders

Exploration and Development of (tib + TiC)/Ti6Al4V Through the Economically Viable Melt Hydrogenation Technique

Microstructure and mechanical properties of an in-situ TiB2 particle reinforced AlSi10Mg composite additive manufactured by selective electron beam melting

Microstructure and Mechanical Properties of Ti-TiH2 Based Matrix Composites Reinforced with xTiB2 Particles Processed by Powder Metallurgy

Microstructure and Mechanical Properties of Ti-TiBw-x%Cu Composites by Powder Metallurgy Using Atomized Ti-TiBw Powder As Raw Materials

Microstructure and Mechanical Properties of an In-Situ TiB 2 Particle Reinforced AlSi10Mg Composite Additive Manufactured by Selective Electron Beam Melting

Synthesis of Al7075/TiB2-Al2O3 In-Situ Hybrid Composite by Stir Casting Method

Microstructural Aspects of In-Situ TiB Reinforced Ti–6Al–4V Composite Processed by Spark Plasma Sintering

Preparation of TiBw/Ti–6Al–4V Composite with an Inhomogeneous Reinforced Structure by a Canned Hot Extrusion Process

Effects of Melt Hydrogenation on the Microstructure Evolution and Hot Deformation Behavior of TiBw/Ti-6Al-4V Composites

Microstructural Characterization and Mechanical Properties of (tib + TiC) Reinforced Ti–6Al–4V Prepared by Melt Hydrogenation

Microstructure Evolution and Mechanical Behavior of TiB-Reinforced Ti-6.5Al-2Zr-1Mo-1V Matrix Composites Obtained by Vacuum Arc Melting and Spark Plasma Sintering

A Novel Fabrication Technology of in Situ TiB2/6063Al Composites: High Energy Ball Milling and Melt in Situ Reaction

Densification behavior, mechanical and electrical properties of in-situ TiB 2p /Cu composite powder via vacuum hot pressing