Effect of epoxy material itself on characteristics and properties of its fluorinated surface layer

B. Niu,F. Ma,Z. Xiang,X. Liu,Z. An

DOI: https://doi.org/10.1049/icp.2022.0255

2021-01-01

Abstract:In order to investigate a possible effect of the epoxy material itself on physicochemical characteristics and electrical properties of the fluorinated surface layer, in this report, three kinds of anhydride cured epoxy samples were prepared using different raw materials and formulations and. Their surface fluorination was performed in a laboratory stainless vessel under the same conditions. ATR-IR analysis shows a stronger C=O absorption for the sample with a higher crosslink density, and also indicates that fluorine atoms are incorporated into the surface layers. SEM cross-section images show a thicker fluorinated layer for the sample with a lower crosslink density. SEM surface images indicate that the fluorination led to the formation of many surface cracks and/or pits, and surface cracks are much deeper for the sample with a higher crosslinking density. The measurements of surface conductivity and surface potential decay reveal a significant increase in surface conductivity or the potential decay rate for these epoxy samples by the fluorination. The measurements also show a significant dependence of the increase in surface conduction on the resin raw materials and formulation, and the higher the epoxy value or crosslinking density, the more the increase in surface conduction.