Electrochemical Behaviors of Environment Friendly Conversion Coating Formed on Mg Alloys

Wanqiu Zhou,Qiang Zhao,Li Sheng,Xin Li,Shiwei Wu

DOI: https://doi.org/10.1149/ma2014-03/5/542

2014-01-01

ECS Meeting Abstracts

Abstract:Introduction The application of magnesium alloys has increased steadily in automobile industry and electric appliance because of attractive combination of low density and high strength/weight ratio. However, Mg-based alloys present a unique corrosion protection challenge due to their high chemically reactivity. One of the most effective ways to improve the corrosion resistance of Mg alloys is to form a coating on the surface to isolate the base material from the corrosive circumstance. Traditionally, chromate conversion coatings (CCCs) have been widely used. It has been conscious that Cr(VI) chemicals were carcinogenic and contaminated the circumstance severely. Many alternative non-chromate treatments have been developed based on the baths such as rare earth salt and phosphate compounds[1]. As the alternative technique for chromate treatments, electrochemical behaviors of the obtained conversion coating from manganesephosphate bath has become a major concern. The aim of the presented investigations is to develop a enviroment friendly conversion coating with effective protection for AM 60 magnisium alloys. The corrosion performance of the coating was evaluated by electrochemical technique in 3.5%NaCl, the chemical composition of the coating was analysed by EDX and the surface morphology was observed using SEM. Experimental Cast AM60 magnesium alloy was used as substrate. The main bath ingredient and operating condition for phosphate treatment are given as follow: Manganese dihydro phosphate: 20-50 g/l, H3PO4 (85% wt): 3-10 ml/l, pH: 2.0-3.5, Time: 10-30 min, Temperature: 45-75°C. The addictives added into the treating bath were fluoride and organic acid. Phosphate process for AM60 magnesium alloys included four main steps: mechanical polishing, acetone degrease, activation and phosphate treatment. The specimens were polished from 600grit to 1200grit using emery paper, followed by clean in acetone ultrasonically. Activation was performed by immersion the specimens in NH4HF2 of 50g/l aqueous solution at room temperature for 1-5 minutes. Electrochemical measurements were carried out using EG&G model 273 potentiostat and 5210 amplifier system. A conventional three-electrode polarization cell was adopted, specimen as a working electrode covered with cold setting resin with only 1 cm surface exposed, a saturated calomel electrode (SCE) as a reference electrode and a platinum as counter electrode. The corrosion resistance of the conversion coating was evaluated by polarization curve test at a scan rate of 0.5 mV/s in 3.5% NaCl. Surface morphology of the specimen was observed by environmental scanning electron microscopy(SEM) (Model XL30 FEG), and the specimen composition analysis was conducted by the energy dispersive X-ray (EDX) attached to SEM. Results and discussion Morphologies of conversion coating deposited on AM60 magnesium alloy from manganese-phosphate bath is presented in Fig.1, and the EDX spectrum of the coating is given in Fig.2. The film was compact and the metal substrate was covered with phosphate particles. The bottom grains were relatively of large size, and the crystal grains of small size could be seen produced on the top of the large bottom grains. The peaks appeared in the EDX spectrums corresponding to the chemical elements of O and P as well as Mn respectively which implied that the coating was some kinds of compounds composited of oxygen and phosphor as well as manganese.