Study on structure and properties of microarc oxidation coating on magnesium alloy in phosphate-potassium hydroxide solution

LIANG Jun,TIAN Jun,ZHOU Jin-fang,LIU Wei-min,XU Tao

DOI: https://doi.org/10.3969/j.issn.1004-227X.2005.12.002

2005-01-01

Abstract:The oxidation coating on magnesium alloy surface was obtained from electrolyte of phosphate-potassium hydroxide with microarc oxidation technics.Photos of cross-section optical microscope morphology and SEM show that the oxidation coating is continuous.The clear interface exists between oxidation coating and substrate.There aren't disfigurements of hole and crack existing about interface.Many microholes distribute on the surface of oxidation coating,and there are cracks on it.The EDS components analysis show that the coating consists of Mg,Al(gained from substrate) and P,O(gained from electrolyte).X-ray diffraction experiment proves that the oxidation coating is mostly composed of MgO but without P.It indicates that P forms a non-crystal in the coating.The cross-section hardness distribution curve of coating and corrosion resistant test show that with increasing distance between coating and interface, the coating hardness increases firstly and reaches the maximum value of 580 HV at the distance of 10 μm from interface,and then decreases.Polariration corrosion current density of substrate and microarc coating are 198 A/cm~2 and 3.54 A/cm~2 respectively in the solution of w(NaCl)=(3.5%) NaCl.It shows that the corrosion resistance of magnesium alloy is increased due to the formation of oxidation coating.