Zhiquan Huang,Ruiqiang Wang,Xintong Liu,Dongdong Wang,Heng Zhang,Xiaojie Shen,Dejiu Shen,Dalong Li
Abstract:Coatings prepared by different electrolyte additives were investigated on AZ31 magnesium alloy by plasma electrolytic oxidation. In this study, scanning electron microscopy, energy-dispersive X-ray spectroscopy and X-ray diffraction analysis were employed to assess the morphologies, chemical and phase compositions of the plasma electrolytic oxidation (PEO) coatings, respectively. Furthermore, electrochemical impedance spectroscopy was used to evaluate the corrosion behavior of the composite coating. The investigation of the effect of electrolyte additives in the base electrolyte showed that the PEO specimens exhibit different surface and cross-sectional morphologies, and phase compositions. The results showed that SiO32− was conducive to the growth of the ceramic layer, and the ceramic layer developing in the electrolyte which contained AlO2− showed a typical double-layer structure. The corrosion resistance of coating formed in a phosphate bath was higher than that of the coating formed in silicate bath and coating formed in an aluminate bath. Moreover, the corrosion resistance of the coating formed in the fluoride bath was the highest.
What problem does this paper attempt to address?
The paper attempts to address the impact of different electrolyte additives on the structural characteristics and corrosion resistance of plasma electrolytic oxidation (PEO) coatings on AZ31 magnesium alloy.
### Research Background and Objectives
Magnesium alloys are considered one of the most promising metals for lightweight industrial applications due to their low density, high strength-to-weight ratio, and excellent processing and recycling capabilities. However, due to the poor corrosion resistance of magnesium alloys, there are many limitations in practical applications. To improve the corrosion resistance of magnesium alloys, plasma electrolytic oxidation (PEO) technology has been widely used as an environmentally friendly surface treatment method.
### Research Content
This paper studies the effects of silicate, phosphate, aluminate, and fluoride on the performance of AZ31 magnesium alloy coatings under different electrolyte additive conditions through PEO treatment. The specific experimental design includes:
1. **Electrolyte Composition**: Using an alkaline base electrolyte, different anions (such as SiO₃²⁻, AlO₂⁻, PO₄³⁻, F⁻) were added, with Na⁺ as the cation.
2. **Sample Preparation**: AZ31 magnesium alloy samples with dimensions of 15 mm × 15 mm × 1 mm were polished, cleaned, and ultrasonically degreased, followed by PEO treatment using a pulsed AC power supply.
3. **Characterization Methods**: Scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), and X-ray diffraction (XRD) were used to analyze the morphology, chemical composition, and phase composition of the coatings.
4. **Electrochemical Testing**: The corrosion resistance behavior of the coatings was evaluated by electrochemical impedance spectroscopy (EIS).
### Main Findings
- Different electrolyte additives significantly affected the voltage-time curves, morphology, and thickness of the coatings. Among them, silicate electrolyte was most conducive to the rapid growth of the ceramic layer.
- The silicon coating had the highest voltage and the thickest coating thickness, while the phosphate coating exhibited lower voltage fluctuations and a smooth surface morphology.
- Fluoride coatings showed the best corrosion resistance, followed by phosphate, silicate, and aluminate coatings.
Through the above research, the authors aim to reveal the specific mechanisms by which different electrolyte additives affect the performance of PEO coatings and provide a theoretical basis for further optimization of magnesium alloy surface treatment processes.