Abstract:This study characterizes and determines the corrosion resistance of Mn-Ce conversion coated LZ91 magnesium alloy that undergoes pretreatments. It is challenging to process large and curved workpieces in the industry because the geometric shapes are complex if they are mechanically ground. This study uses acid pickling instead of mechanical grinding, and a nitric acid solution is used for pickling. After pretreatments, the samples are immersed for 30 s in a conversion coating solution containing 0.1 M KMnO4 and 0.025 M Ce(NO3)3 with a pH of 1.5, as demonstrated in previous studies by the authors. The microstructure of the coating layer and electrochemical behavior of conversion coated samples exposed to 3.5 wt.% NaCl solution are studied. The corrosion behavior of Mn-Ce conversion coating specimens is determined using a salt spray test (SST). Scanning electron microscopy (SEM), energy dispersive X-ray spectrometry (EDS), and X-ray photoelectron spectroscopy (XPS) are used to analyze the interface between the coating layer and the underlying magnesium substrate and to investigate the microstructure of the specimens. The roughness of the coatings is measured using 3D white light interferometry. The results show that the deteriorated area ratio for conversion coated LZ91 decreases to less than 5% after 72 h of SST exposure, and the corrosion resistance is improved 2.25 times with the Mn-Ce conversion coating on LZ91 magnesium alloy.

Investigation of the Ce-Mn Conversion Coating on 6063 Aluminium Alloy

Investigation of the trivalent-chrome coating on 6063 aluminum alloy

EIS Investigation of the Deposition of Trivalent Chromium Coatings on Al 6063 Alloy

Investigation on the composition and corrosion resistance of cerium-based conversion treatment by alkaline methods on aluminum alloy 6063

Improved electrochemical performance of trivalent-chrome coating on Al 6063 alloy via urea and thiourea addition

A Chromate-Free and Convenient Route to Fabricate Thin and Compact Conversion Coating for Corrosion Protection on LZ91 Magnesium Alloy

PREPARATION AND CORROSION ELECTROCHEMISTRY BEHAVIOR OF CERIUM-BASED CHEMICAL CONVERSION COATING ON AZ91 MAGNESIUM ALLOY

Preparation and corrosion resistance of titanium–zirconium–cerium based conversion coating on 6061 aluminum alloy

Electrochemical corrosion resistance of aluminum alloy 6101 with cerium-based coatings in an alkaline environment

Cerium and Silane Conversion Coatings on AZ91 Magnesium Alloy

Influence of the Chemical Composition of Ceria Conversion Coatings, Sealed in Solution of NaH2PO4 and Ca(NO3)2, on the Corrosion Behavior of Aluminum

Corrosion resistance and electrical conductivity of V/Ce conversion coating on magnesium alloy AZ31B

Electrochemical Study of Corrosion Behavior of Rare Earth Based Chemical Conversion Coating on Aerospace Aluminum Alloy

STUDY ON THE CORROSION BEHAVIOR OF Ce CONVERSION COATINGS ON Al6061/SiCp COMPOSITES

Amorphous Al–Mn Coating on NdFeB Magnets: Electrodeposition from AlCl3–EMIC–MnCl2 Ionic Liquid and Its Corrosion Behavior

Preparation and Corrosion Behaviour of Cerium Based Sol-gel Composite Coatings on AA2024-T4 Aluminum Alloy

The Preparation, Corrosion Resistance and Formation Mechanism of a New-Type Mo-Based Composite Conversion Coating on 6061 Aluminum Alloy

Formation and characterization analysis of a chromium-free conversion coating on Mg alloy prepared in a Mo-Mn-V based weak acid solution

Preparation and Properties of Mo/Ti/Sn Conductivity Conversion Coatings on 6063 Aluminum Alloy

Enhanced long-term corrosion protection of 2A14 aluminum alloy: Hybrid effect of micro-arc oxidation coating and cerium based conversion treatment