Improved corrosion resistance of Mg alloy by a green phosphating: insights into pre-activation, temperature, and growth mechanism

Tao Li,Shifang Wang,Hongtao Liu,Jianhua Wu,Shouqiu Tang,Yuansheng Yang,Xitao Wang,Jixue Zhou

DOI: https://doi.org/10.1007/s10853-020-05288-w

IF: 4.5

2020-09-14

Journal of Materials Science

Abstract:Poor corrosion resistance of magnesium alloys remains a major obstacle to their extensive application. Phosphate conversion coating (PCC) is one of the most direct and effective strategies to enhance the corrosion resistance of magnesium alloys. To overcome the environmental damage of traditional phosphating technology, a PCC free of fluorine, chromium and nitrite was prepared in the present work. The effects of surface pre-activation process and preparation temperature on the surface morphology and corrosion resistance of PCC on ZK60 magnesium alloy were investigated. Surface pre-activation could significantly reduce the ultimate grain size of phosphate. At 90 °C, the prepared PCC showed perfect morphology and corrosion resistance. To better understand the phosphating nucleation and growth process, the surface and cross-sectional morphologies of PCC prepared for different times were observed. The phase composition of the prepared PCC was detected to be Hureaulite (Mn5(PO4)2(PO3OH)2·4H2O) and the coating growth mechanism was suggested in the end.

materials science, multidisciplinary

What problem does this paper attempt to address?

### Problems the Paper Aims to Solve

This paper aims to enhance the corrosion resistance of magnesium alloys by developing a phosphate conversion coating (PCC) that is free of fluorine, chromium, and nitrites. Specifically:

1. **Environmentally Friendly Phosphate Conversion Coating**:
- Traditional phosphate technology typically adds fluorine, chromium, and nitrites to enhance protective capabilities in engineering applications, but these components cause severe environmental damage. Therefore, researchers have developed a new type of phosphate conversion coating that does not contain these harmful components.

2. **Improving Corrosion Resistance of Magnesium Alloys**:
- Magnesium alloys have a wide range of applications due to their excellent lightweight properties, but their poor corrosion resistance limits their widespread use. The paper aims to improve the corrosion resistance of magnesium alloys by studying new phosphate conversion coatings.

3. **Impact of Surface Pre-activation Process**:
- Studies have shown that surface pre-activation treatment can significantly reduce the grain size of phosphate crystals, thereby improving the density and uniformity of the coating. By comparing samples with and without pre-activation treatment, it was found that the phosphate crystals formed after pre-activation treatment are finer, and the coating thickness is also reduced.

4. **Effect of Preparation Temperature on Coating Performance**:
- Research has found that different preparation temperatures have a significant impact on the morphology and corrosion resistance of phosphate coatings. Coatings prepared at 90°C exhibit the best morphology and corrosion resistance, with a grain size of 15 micrometers, and the coating is very dense.

5. **Study of Phosphate Conversion Mechanism**:
- By observing phosphate coatings prepared at different times, the nucleation and growth process of phosphate was studied, and the corresponding phosphate conversion mechanism was proposed. It was finally determined that the main component of the phosphate coating is Hureaulite (Mn5(PO4)2(PO3OH)2/C14H2O).

In summary, this paper aims to improve the corrosion resistance of magnesium alloys by developing an environmentally friendly phosphate conversion coating and conducts detailed studies on its surface pre-activation process, preparation temperature, and conversion mechanism.