Abstract:Introduction The application of magnesium alloys has increased steadily in automobile industry and electric appliance because of attractive combination of low density and high strength/weight ratio. However, Mg-based alloys present a unique corrosion protection challenge due to their high chemically reactivity. One of the most effective ways to improve the corrosion resistance of Mg alloys is to form a coating on the surface to isolate the base material from the corrosive circumstance. Traditionally, chromate conversion coatings (CCCs) have been widely used. It has been conscious that Cr(VI) chemicals were carcinogenic and contaminated the circumstance severely. Many alternative non-chromate treatments have been developed based on the baths such as rare earth salt and phosphate compounds[1]. As the alternative technique for chromate treatments, electrochemical behaviors of the obtained conversion coating from manganesephosphate bath has become a major concern. The aim of the presented investigations is to develop a enviroment friendly conversion coating with effective protection for AM 60 magnisium alloys. The corrosion performance of the coating was evaluated by electrochemical technique in 3.5%NaCl, the chemical composition of the coating was analysed by EDX and the surface morphology was observed using SEM. Experimental Cast AM60 magnesium alloy was used as substrate. The main bath ingredient and operating condition for phosphate treatment are given as follow: Manganese dihydro phosphate: 20-50 g/l, H3PO4 (85% wt): 3-10 ml/l, pH: 2.0-3.5, Time: 10-30 min, Temperature: 45-75°C. The addictives added into the treating bath were fluoride and organic acid. Phosphate process for AM60 magnesium alloys included four main steps: mechanical polishing, acetone degrease, activation and phosphate treatment. The specimens were polished from 600grit to 1200grit using emery paper, followed by clean in acetone ultrasonically. Activation was performed by immersion the specimens in NH4HF2 of 50g/l aqueous solution at room temperature for 1-5 minutes. Electrochemical measurements were carried out using EG&G model 273 potentiostat and 5210 amplifier system. A conventional three-electrode polarization cell was adopted, specimen as a working electrode covered with cold setting resin with only 1 cm surface exposed, a saturated calomel electrode (SCE) as a reference electrode and a platinum as counter electrode. The corrosion resistance of the conversion coating was evaluated by polarization curve test at a scan rate of 0.5 mV/s in 3.5% NaCl. Surface morphology of the specimen was observed by environmental scanning electron microscopy(SEM) (Model XL30 FEG), and the specimen composition analysis was conducted by the energy dispersive X-ray (EDX) attached to SEM. Results and discussion Morphologies of conversion coating deposited on AM60 magnesium alloy from manganese-phosphate bath is presented in Fig.1, and the EDX spectrum of the coating is given in Fig.2. The film was compact and the metal substrate was covered with phosphate particles. The bottom grains were relatively of large size, and the crystal grains of small size could be seen produced on the top of the large bottom grains. The peaks appeared in the EDX spectrums corresponding to the chemical elements of O and P as well as Mn respectively which implied that the coating was some kinds of compounds composited of oxygen and phosphor as well as manganese.

Tuning the nucleation kinetics of phosphate chemical conversion coating on Mg-Gd-Y-Zr magnesium alloy: The effect of pretreatment and organic additive

Effects of nucleation pretreatment on corrosion resistance of conversion coating on magnesium alloy Mg-10Gd-3Y-0.4Zr

Preparation and Characterization of Mg-P Coatings on Mg-Zn-Y-Nd Alloy for Corrosion Protection

Structure and Formation Mechanism of Phosphate Conversion Coating on Die-Cast Az91d Magnesium Alloy

The Study of a Phosphate Conversion Coating on Magnesium Alloy AZ91D: III. Nano-particle Modification

Effect of Ph Value and Preparation Temperature on the Formation of Magnesium Phosphate Conversion Coatings on AZ31 Magnesium Alloy

Preparation of Conductive and Corrosion Resistant Phosphate Conversion Coating on AZ91D Magnesium Alloy

Electrochemical Behaviors of Environment Friendly Conversion Coating Formed on Mg Alloys

Grain Refinement Promotes the Formation of Phosphate Conversion Coating on Mg Alloy AZ91D with High Corrosion Resistance and Low Electrical Contact Resistance

Probing the effect of microstructural difference of AZ91D magnesium alloys on the corrosion resistance of phosphate conversion coatings

Improved corrosion resistance of Mg alloy by a green phosphating: insights into pre-activation, temperature, and growth mechanism

Preparation of Composite Molybdate/Phosphate Conversion Coating on Mg Alloys

Chemically depleting the noble impurities from AZ91-T4 magnesium alloy: A new and efficient pretreatment method to improve the corrosion resistance of phosphate conversion coatings

Nano Al2O3/phosphate composite conversion coating formed on magnesium alloy for enhancing corrosion resistance

Barium Phosphate Conversion Coating on Die-Cast AZ91D Magnesium Alloy

A Green Conversion Coating on a Magnesium Alloy for Corrosion Protection

Preparation and Corrosion Behaviors of Calcium Phosphate Conversion Coating on Magnesium Alloy

Zinc Phosphate Coating on the Surface of AZ91D Mg Alloy

Influence of Additive on Structure and Corrosion Resistance of Manganese Phosphate Film on Az91 Magnesium Alloy

Evaluation of electrochemical and surface characteristics of conversion coatings on ZM21 magnesium alloy

Phosphate Conversion Coating on Diecast AZ91D and Its Corrosion Resistance