Abstract:This study reports the fatigue failure mechanism at very -high -cycle fatigue (VHCF) regime of laser powder bed fusion (LPBF) GH4169 superalloy through a series of detailed microstructural characterizations, including scanning electron microscopy (SEM), transmission electron microscopy (TEM), electron backscatter diffraction (EBSD), and energy dispersive spectrometer (EDS). Microstructural characterization of the solution and doubleaging post -treated initial material exhibits process -induced imperfections (mainly pores), as well as gamma ' , gamma '' and delta precipitates, and carbide. The fatigue tests were performed using an ultrasonic fatigue tester (20 kHz). Fatigue fracture analysis suggests there exists a competitive fatigue failure mechanism with surface flaw initiation and internal pore initiation, corresponding to high -cycle fatigue (HCF) and VHCF regime, respectively. Focused ion beam (FIB) samples taken within the fatigue initiation area (FIA) revealed grain refinement and precipitate dissolution behavior. Based on the characterization results, the fatigue crack initiation mechanism was hypothesized: During numerous cyclic loading, the mobile dislocations shear gamma ' and gamma '' precipitates, causing their dissolution and local chemical and mechanical alterations near internal pores. This enables twinning and promotes sub -grains formation. Sub -grains refine via localized continuous dynamic recrystallization (CDRX), forming a fine-grained layer that leads to crack initiation. This work reveals how precipitate dissolution contributes to VHCF crack initiation in LPBF GH4169 superalloy, highlighting the potential for extending alloy lifespan by adjusting precipitates and LPBF defects and incorporating these factors into fatigue life predictions for enhanced accuracy.

Revealing the Fatigue Crack Propagation Mechanism of a Ni-based Superalloy Electron Beam Welded Joint Through In-Situ SEM Observation

Effect of texture evolution and defect on the crack initiation of a Ni‐based superalloy electron beam welded joint

In-situ SEM study of short fatigue crack propagation behavior in a dissimilar metal welded joint of nuclear power plant

Microstructural insights into fatigue short crack propagation resistance and rate fluctuation in a Ni-based superalloy manufactured by Laser powder bed fusion

Fatigue crack growth behavior of Ni-Cr-Mo-V steel welded joints considering strength mismatch effect

On fatigue crack path deviation at elevated temperature in electron beam repaired weldments of turbine disk

In-situ investigation of microstructure-dependent deformation behavior of an electron-beam welded Ni Co based superalloy

Analysis on the Microfissuring Behavior in the Heat-affected Zone of Electron-beam Welded Nickel-based Superalloy

Microstructure and Mechanical Properties of Inconel713C Ni3Al-based Superalloy Joint Welded by Electron Beam Feeding Wire Welding Technology

Mechanisms Affecting the Difference in Fatigue Resistance Between Welds and Base Materials Were Investigated Based on In-Situ Fatigue Method

Microstructural Evolution and Formation of Fine Grains During Fatigue Crack Initiation Process of Laser Powder Bed Fusion Ni-based Superalloy

Microstructure and Properties of 3D-GH3625 Electron beam welded

Creep Behavior and Fracture Mechanisms of the Dissimilar Inertia Friction Welded Joints of Deformed and Powder Metallurgy Ni‐Based Superalloys

High-Temperature Fatigue Behavior of Inertia Friction Welded Joints of GH4065A Ni-Based Superalloy

Fatigue Crack Growth Mechanism of Ni-based Weld Metal in a 9% Ni Steel Joint

Fatigue crack initiation behaviors around defects induced by welding thermal cycle in superalloy IN617B

Fatigue Fracture Mechanism of a Nickel-Based Single Crystal Superalloy with Partially Recrystallized Grains at 550 C by In Situ SEM Studies

Stray grain formation, thermomechanical stress and solidification cracking in single crystal nickel base superalloy welds

Microstructure and Mechanical Properties of the IC10/GH3039 Dissimilar Electron Beam Welded Joint

Explore the mechanism of high fatigue crack propagation rate in fine microstructure of friction stir welded aluminum alloy

Fatigue behaviour of a laser beam welded CoCrFeNiMn-type high entropy alloy