Enhanced Energy‐Storage Properties and Good Temperature Stability in 0.92(sr0.7bi0.2)tio3–0.08bi(mg0.5hf0.5)o3 Relaxor Ferroelectric Ceramic

Xi Kong,Letao Yang,Zhenxiang Cheng,Shujun Zhang

DOI: https://doi.org/10.1002/aesr.202100015

2021-01-01

Advanced Energy and Sustainability Research

Abstract:Herein, the (1 − x)(Sr0.7Bi0.2)TiO3–xBi(Mg0.5Hf0.5)O3 (SBT–100xBMH, x = 0.04–0.10) relaxor ferroelectric ceramics are fabricated via the high‐temperature solid‐state reaction method. Dielectric and ferroelectric measurements reveal a typical relaxor characteristic with diffused and frequency‐dependent dielectric peaks. The characteristic Weibull breakdown strength (BDS) of 470 kV cm−1 with satisfied reliability is obtained by DC breakdown measurement. A maximum recoverable energy density of 3.5 J cm−3 with the corresponding energy efficiency of 92% is simultaneously achieved at 380 kV cm−1. The recoverable energy density exhibits minor degradations from ambient temperature to 200 °C with variation below 20%, whereas the energy efficiency is maintained above 90%. In addition, the SBT–8BMH ceramic possesses a fast charge–discharge speed with high discharge power density of 2.9 MW cm−3. All the results make this lead‐free relaxor ferroelectric ceramic a promising potential candidate for high‐temperature energy‐storage capacitor applications.