Understanding the Hydrogen Effect on Pop-in Behavior of an Equiatomic High-Entropy Alloy During In-Situ Nanoindentation

Dong Wang,Xu Lu,Meichao Lin,Di Wan,Zhiming Li,Jianying He,Roy Johnsen
DOI: https://doi.org/10.1016/j.jmst.2021.04.060
2022-01-01
Abstract:The variations in the pop-in behavior of an equiatomic CoCrFeMnNi high-entropy alloy under different hydrogen charging/discharging conditions were characterized via in-situ electrochemical nanoindentation. Results show that hydrogen accumulatively reduces both pop-in load and width, among which the reduction of pop-in width is more noticeable than that of pop-in load. Moreover, the hydrogen reduction effect on both pop-in load and width is reversible when hydrogen is degassed during anodic discharging process. Particularly, the hydrogen-reduced pop-in width was studied in detail by a comprehensive energy balance model. It is quantitatively shown that the dissolved hydrogen enhances lattice friction, leading to an increased resistance to dislocation motion. As a result, fewer dislocations can be generated with a higher hydrogen concentration, causing a smaller pop-in width. This is the first time that the pop-in width indicated dislocation mobility under hydrogen impact is quantitively revealed.
What problem does this paper attempt to address?