Abstract:We report a systematic computational analysis of the mechanical behavior of plasma-facing component (PFC) tungsten focusing on the impact of void and helium (He) bubble defects on the mechanical response beyond the elastic regime. Specifically, we explore the effects of porosity and He atomic fraction on the mechanical properties and structural response of PFC tungsten, at varying temperature and bubble size. We find that the Young modulus of defective tungsten undergoes substantial softening that follows an exponential scaling relation as a function of matrix porosity and He atomic content. Beyond the elastic regime, our high strain rate simulations reveal that the presence of nanoscale spherical defects (empty voids and He bubbles) reduces the yield strength of tungsten in a monotonically decreasing fashion, obeying an exponential scaling relation as a function of tungsten matrix porosity and He concentration. Our detailed analysis of the structural response of PFC tungsten near the yield point reveals that yielding is initiated by emission of dislocation loops from bubble/matrix interfaces, mainly 1/2⟨111⟩ shear loops, followed by gliding and growth of these loops and reactions to form ⟨100⟩ dislocations. Furthermore, dislocation gliding on the ⟨111⟩{211} twin systems nucleates 1/6⟨111⟩ twin regions in the tungsten matrix. These dynamical processes reduce the stress in the matrix substantially. Subsequent dislocation interactions and depletion of the twin phases via nucleation and propagation of detwinning partials lead the tungsten matrix to a next deformation stage characterized by stress increase during applied straining. Our structural analysis reveals that the depletion of twin boundaries (areal defects) is strongly impacted by the density of He bubbles at higher porosities. After the initial stress relief upon yielding, increase in the dislocation density in conjunction with decrease in the areal defect density facilitates the initiation of dislocation-driven deformation mechanisms in the PFC crystal.

Effect of Hydrogen on the Slip Resistance of Tungsten Single Crystals

Hydrogen Behaviors at the Near-Surface Region of Tungsten: A First-Principles Study

Nanostructure Evolution and Surface Modification of Tungsten Exposed to Low Energy, High Flux Deuterium Plasma

Hydrogen retention and affecting factors in rolled tungsten: Thermal desorption spectra and molecular dynamics simulations

Crystal orientation effects on helium ion depth distributions and adatom formation processes in plasma-facing tungsten

The effect of hydrogen on dislocation motion and cracking in tungsten foil

Molecular dynamics modelling of the stress effect on diffusion behavior of hydrogen in tungsten

Effect of Surface Quality on Hydrogen/helium Irradiation Behavior in Tungsten

Nucleation Mechanism of Intra-Granular Blisters in Tungsten Exposed to Hydrogen Plasma

Defect production in tungsten under sub-threshold energy irradiation: Role of hydrogen and surface effects

Impact of helium and hydrogen plasma exposure on surface damage and erosion of tungsten

Deuterium-induced Nanostructure Formation on Tungsten Exposed to High-Flux Plasma

Study of interaction between low energetic hydrogen and tungsten surface by molecular dynamics simulations

Effects of Deuterium Plasma Exposure and Helium Ions Irradiation on Nanoindentation Hardness of Tungsten

Deuterium behavior in tungsten exposed to deuterium plasma with rising or declining temperature

Irradiation hardening induced by blistering in tungsten due to low-energy high flux hydrogen plasma exposure

Effect of initial exposure temperature on the deuterium retention and surface blistering in tungsten

Initial growth of tungsten fuzz induced by bubble-driven surface stress layer under helium irradiation

Hydrogen Distribution Induced Screw Dislocation Core Spreading in Tungsten

Molecular-Dynamics Analysis of the Mechanical Behavior of Plasma-Facing Tungsten

Helium effects on the surface and subsurface evolutions in single-crystalline tungsten