Abstract:High-manganese twinning-induced plasticity (TWIP) steels exhibit high strain hardening, high tensile strength, and high ductility, which make them attractive for structural applications. At low tensile strain rates, TWIP steels are prone to hydrogen embrittlement (HE). Here though, we study the hardening and strengthening resulting from electrochemical hydrogen-charging of a surface layer of a Fe-26.9Mn-0.28C (wt.%) TWIP steel. We observed a 20% increase in yield strength following the electrochemical hydrogen-charging, accompanied by a reduction in ductility from 75% to 10% at a tensile strain rate of 10−3s−1. The microstructural evolution during tensile deformation was examined at strain levels of 3%, 5% and 7% by electron backscatter diffraction (EBSD) and electron channeling contrast imaging (ECCI) to study the dislocation structure of the hardened region. As expected, the microstructure of the hydrogen-hardened and the uncharged regions of the material evolve differently. The uncharged areas show entangled dislocation structures, indicating slip from a limited number of potentially coplanar slip systems. In contrast, hydrogen segregated to the grain boundaries, revealed by the deuterium-labelled atom probe tomography, delays the dislocation nucleation by blocking dislocation sources at the grain boundaries. The charged areas hence first show the formation of cells, indicating dislocation entanglement from more non-coplanar slip systems. With increasing strain, these cells dissolve, and stacking faults and strain-induced ε-martensite are formed, promoted by the presence of hydrogen. The influence of hydrogen on dislocation structures and the overall deformation mechanism is discussed in details.

Reveal Hydrogen Behavior at Grain Boundaries in Fe–22Mn–0.6C TWIP Steel via In Situ Micropillar Compression Test

Interaction Between Dislocations, Precipitates and Hydrogen Atoms in a 2000 MPa Grade Hot-Stamped Steel

Hydrogen-induced hardening of a high-manganese twinning induced plasticity steel

Observation of the Hydrogen-Dislocation Interactions in a High-Manganese Steel after Hydrogen Adsorption and Desorption

Effect of manganese content on the hydrogen embrittlement of twinning-induced plasticity (TWIP) steels under hydrogen charging and hydrogen environment

Hydrogen embrittlement resistance of TWIP (twinning-induced plasticity) steel in high pressure hydrogen environment

Atomic scale understanding of the role of hydrogen and oxygen segregation in the embrittlement of grain boundaries in a twinning induced plasticity steel

Hydrogen embrittlement of twinning-induced plasticity steels: Contribution of segregation to twin boundaries

Hydrogen-enhanced densified twinning (HEDT) in a twinning-induced plasticity (TWIP) steel

Unveiling the Origin of Work Hardening Behavior in an Ultrafine-Grained Manganese Transformation-Induced Plasticity Steel by Hydrogen Investigation

Hydrogen-enhanced microbanding in an austenitic FeMnAlC low-density steel: Effect on hydrogen embrittlement resistance

Effect of pre-strain on hydrogen embrittlement of high manganese steel

Influence of Hydrogen and Annealing Process on the Microstructural Evolution and Fracture Micromechanisms of Medium Mn Steel: an In-Situ TEM Investigation

Investigation of Hydrogen Influencing Γ-Phase True and Pseudo Twinning in a TiAl Based Alloy During High-Temperature Plane Strain Compression

Twinning behavior and hydrogen embrittlement of a pre-strained twinning-induced plasticity (TWIP) steel

Solute Hydrogen Effects on Plastic Deformation Mechanisms of Α-Fe with Twist Grain Boundary

Effect of pre-strain on critical conditions for hydrogen-induced delayed cracking and crack nucleation characteristic of DP1180 steel

In-situ investigation of the interaction between hydrogen and stacking faults in a bulk austenitic steel

Effects of heterogeneous plastic strain on hydrogen-induced cracking of twinning-induced plasticity steel: A quantitative approach

Hydrogen Trapping Sites and Hydrogen-Induced Cracking in High Strength Quenching & Partitioning (Q&P) Treated Steel

Hydrogen Traps And Hydrogen Induced Cracking In 20crmo Steel