Dual-interstitials promoted multiple mechanisms enhance strength-ductility synergy of an equiatomic high-entropy alloy
Yuefeng Hu,Kefu Gan,Yong Zhang,Dingshun Yan,Qiankun Yang,Shuya Zhu,Zhiming Li
DOI: https://doi.org/10.1016/j.jallcom.2023.172271
IF: 6.2
2023-09-24
Journal of Alloys and Compounds
Abstract:Although minor additions of interstitials have been employed to enhance the yield strength of high-entropy alloys (HEAs) with multi-principal elements, the significant loss of ductility occurs as the cost. In this work, to further improve strength-ductility synergy of the model face-centered cubic (FCC) CoCrFeMnNi HEA, dual-interstitial alloying of C and N is manipulated with the emphasis on tuning the microstructures and multiple strengthening mechanisms. C (0.6 at%) and N (0.8 at%) are completely dissolved in the FCC matrix after annealing at or above 1150 °C. The dissolution of the dual-interstitials in the matrix refines grains by impeding grain boundary migration via solute atmospheres. Nanoprecipitates including M 23 C 6 , Cr 3 C 2 and Cr 2 (N, C) are dispersed in the recrystallized FCC matrix of the dual-interstitial HEAs upon annealing at 950–1000 °C. The Zener pinning pressure induced by these nanoprecipitates retards grain boundary migration and hence reduces grain sizes. The primary deformation mechanism is dislocation slip in both dual-interstitial HEAs with and without precipitates at the early deformation stages (e.g., 40% local strain), the mechanical twinning occurs at the medium and late deformation stages (e.g., 60% and 90% local strains, respectively) contributing to the high ductility of the HEAs. The synergetic strengthening effects of nanoprecipitates, grain boundaries, interstitial and substitutional solid-solution brings about high yield strength of 772 MPa and ultimate tensile strength of 1178 MPa at a large elongation of 34% in the dual-interstitial HEA containing carbides/carbonitrides nanoprecipitates. The contributions of the multiple mechanisms are quantified and discussed.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering