Experimental Measurement on the Phase Equilibria of the Mg–Ag–Cu Ternary System at 350 and 400 °C

Jian Wang,Zhang,Yinju Zhang,Liling Jin,Liyuan Sheng

DOI: https://doi.org/10.1016/j.jma.2020.12.019

IF: 11.813

2022-01-01

Journal of Magnesium and Alloys

Abstract:The phase equilibria of the Mg–Ag–Cu ternary system at 350 and 400 °C were experimentally investigated using twenty-eight key samples.The phase equilibria and compositions in key samples were investigated using scanning electron microscopy（SEM） equipped with energydispersive spectroscopy（EDS）. Powder X-ray diffraction（XRD） technique was used to analyze the crystal structure and solid solubility of compounds. Five three-phase equilibria and several two-phase equilibria have been determined at 350 and 400 °C. The solid solubility range of Cu in the compounds Mg 3 Ag, Mg Ag and fcc（Ag） were examined at 350 and 400 °C. The maximum solid solubility of Ag in the compound MgCu 2 was found to be 11.46 at.% and 11.25 at.% with a constant value of about 66 at.% Cu at 350 and 400 °C, respectively.Besides, the solid solubility limits of Ag in the compounds Mg 2 Cu and fcc（Cu） were found to be less than 5 at.% at 350 and 400 °C. No ternary compound was observed in the present work.