Abstract:In the field of condensed matter physics and materials science, it is of great importance to investigate the microstructures, properties and solidification regularities of liquid metals. In the last few decades, the theories of solidification of binary alloys, such as dendritic growth and eutectic growths have been built. Great progress has also been made on the study of monetectic and peritectic alloys. But a solidification theory on ternary quasiperitectic alloys has not been established up to now. The study of the solidification process of quasiperitectic alloys will provide a basic work for solidification theories of ternary alloys.The master alloy of Al-11.8Cu-24.22Mg was prepared from pure Al (99.99%), pure Mg (99.99%) and Al-54.2Cu in a resistance furnace under CO2 and SF6 (volume proportion is 40 : 1) atmosphere. The melted alloy (840-850 degrees C) was pouring into different quenching graphite crucibles at the same time, and the cooling curves were recorded by a sixteen channels temperature recorder. The graphite crucible was quenched into cold-water immediately for rapid cooling at the preplanned quenching temperature. After the experiment, the microstructures of the sample were analyzed by SEM, with EDS analysis.The experiment result indicates that the primary phase is identified as S (Al2CuMg) and the quasiperitectic phases are alpha-Al and T (Al6CuMg4). The solidification microstructure is composed of remnant primary phase, quasiperitectic phases, binary eutectic and ternary eutectic. Although the quasiperitectic phases and binary eutectic are composed of the same phases (alpha-Al+T(Al6CuMg4)), their structures are different. The former structure presents strip form and the later present dendritic form. The ternary eutectic reaction is suppressed and the remnant primary S phase is reserved in the matrix with non-equilibrating crystallization.

Experimental investigation and thermodynamic modeling of the Mg-Cu-Ca ternary system

Experimental Determination of the Phase Equilibrium in the Mg–Cu–Ca Ternary System at 350 °C

Experimental and Thermodynamic Study of the Mg-Sn-Ca-Sr Quaternary System: Part I-Mg-Sn-Ca Ternary System

Experimental Investigation and Thermodynamic Modeling of the Mg–Sn–Sr Ternary System

Thermodynamic study of the Ca-Cu-Zn ternary system with key experimental measurements

Experimental Investigation and Thermodynamic Calculation of Phase Equilibria in the Mg-Pb-Sn Ternary System

Thermodynamic description and simulation of solidification microstructures in the Cu–Mg–Zn system

Experimental Measurement on the Phase Equilibria of the Mg–Ag–Cu Ternary System at 350 and 400 °C

Experimental investigation and thermodynamic assessment of the Mg–Gd–Ag system focused on Mg-rich region

Experimental Investigation of Isothermal Sections and Thermodynamic Modeling on the Cu-Nb-Ni System

Experimental Investigation and Thermodynamic Assessment of Phase Equilibria at the Ti-Mn side in the Ti-Mn-Mo Ternary System

Thermodynamic Modeling of the Ta–Mo–C Ternary System

Thermodynamic Calculation of Phase Equilibria in the C-Mo-Zr System

Liquidus Projection and Thermodynamic Modeling of Sn–Zn–Cu Ternary System

Thermodynamic Descriptions of the Quaternary Mg–Al–Zn–Sn System and Their Experimental Validation

Experimental investigation and thermodynamic modeling of the Mo-Co-B ternary system

Solidified microstructure and Phase equilibria of the Cu–Cr–X (X=Mg, Y) ternary systems

Studies on the thermodynamic and the miscibility gap of the Cu 2O-Al2O3-SiO2 pseudo-ternary system

Investigation on the crystal structure and mechanical properties of the ternary compound Mg11-xZnxSr combined with experimental measurements and first-principles calculations

Solidification Mechanism of Ternary Quasi-Peritectic Alloy of Al-11.8cu-24.22mg

Thermodynamic Modeling of the Ni–Nb–V Ternary System