Organic Light-Emitting Devices Based on Novel Hole Transport Layer
Shuangling Lou,Junsheng Yu,Weizhi Li,Qing Li,Jun Wang,Yadong Jiang
DOI: https://doi.org/10.3321/j.issn:0253-2239.2007.08.022
2007-01-01
Abstract:Double-layer organic light-emitting devices were fabricated by conventional vacuum deposition method using 2, 7-bis (p-methoxyphenyl-m′-tolylamino)-9, 9-dimethylfluorene (TPF-OMe) and N, N′-bipheny 1-N, N′-bis-(3-methylphenyl)-1, 1′-biphenyl-4, 4′-diamine (TPD) as hole transport layer (HTL), respectively, and tris (8-hydroxyquinolinato) aluminum (Alq 3) as electron transport and light emitting layer (ETL and EML). The devices consisting of TPF-OMe as HTL show higher current density but lower luminous efficiency, and a green-blue emission at 516 nm, CIE (0.30, 0.53), which is Alq 3 electroluminescence spectrum. The devices with the structure of ITO/ TPF-OMe (40 nm)/2, 9-dimethyl-4, 7-dipheny 1-1, 10-phenanthroline (bathocuproine or BCP) (5 nm)/Alq 3 (35 nm)/Mg:Ag (300 nm) was also fabricated, which showed blue light emission of TPF-OMe at the peak of 414 nm, CIE coordinates of (0.20, 0.24), current density of 1137 mA/cm 2 and luminance of 900 cd/m 2 at 15 V, the maximum luminous efficiency 0.11 lm/W at 3 V. Also, the devices based on TPF-OMe has 20°C higher thermal stability compared with that using TPD as HTL, which may be caused by the 19°C higher glass-transition temperature (T g) of TPF-OMe than TPD material.