Effect of Microstructure on Local Strain Hardening Behavior along an Equal Toughness Matching Welded Joint of a 30cr2ni4mov Welded Rotor

Yang Guo,Bo ZHU,Zeyu LI,Tong WANG,Jianxun ZHANG,Jiankun XIONG

DOI: https://doi.org/10.2139/ssrn.4057974

2022-01-01

SSRN Electronic Journal

Abstract:Subzone tensile tests were used to quantitatively study the tensile properties along the equal toughness welded joint of a 30Cr2Ni4MoV steel ultra-supercritical steam turbine rotor. The results show that the weld metal (WM) has lower strength than the base metal (BM) but similar plasticity and work hardening properties; the heterogeneous microstructure of the heat-affected zone (HAZ) results in a gradient distribution of tensile properties. By fitting the stress-plastic strain curve based on the Hollomon equation, there are two hardening exponents n 1 and n 2 in each subzone of the welded joint. Based on the K–M curve of the hardening rate, during uniform plastic deformation before necking, the coarse-grained HAZ (CGHAZ) only experienced two work hardening stages III and IV, and other micorregions of the welded joint exhibited three work hardening stages III ~V. The exponent n 1 represents initial hardening stage III when the plastic strain is less than 0.003, and n 2 represents hardening stages IV~V when the plastic strain is greater than 0.003. The uneven distribution of the exponent n 2 along the joint is related to the differences in the microstructure (tempered martensite or bainite) and carbides. Observing the subzone specimens after tensile testing by TEM, it can be found that dislocation cells appeared in the tempered bainite matrix, which had better work hardening capability than tempered martensite. The lath martensite and granular bainite mixed microstructure and fine granular martensite are beneficial for improving the hardening capabilities and delaying the hardening period, but the carbides distributed in the high-angle grain boundaries are not conducive to strain hardening. The microstructure type, grain size and carbides dispersed in the matrix are the main factors affecting the hardening behavior of each subzone of the joint. The strength prediction model of welded joint subzones based on the hardness and the hardening exponent was established.