Abstract:Carbon fiber reinforced silicon carbide matrix composites (C/SiC) have emerged as key materials for thermal protection systems owing to their high strength-to-weight ratio, high-temperature durability, resistance to oxidation, and outstanding reliability. However, manufacturing defects deteriorate the mechanical response of these composites under extreme thermal-force coupling conditions, prompting significant research attention. This study demonstrates a customized in situ loading device compatible with synchrotron radiation facilities, enabling high spatial and temporal resolution recording of internal material damage evolution and failure behavior under thermal-force coupling conditions. Infrared thermal radiation units in a confocal configuration were used to create ultra-high-temperature environments, offering advantages of compactness, rapid heating, and versatility. In situ tensile tests were conducted on C/SiC samples in a nitrogen atmosphere at both room temperature and 1200 °C. The high-resolution image data demonstrate various failure phenomena, such as matrix cracking and pore linkage. Image-based finite element simulations indicate that the temperature-dependent variation of the failure mechanism is attributable to thermal residual stresses and defect-induced stress concentrations. This work seamlessly integrates extreme mechanical testing methods with in situ observation techniques, providing a comprehensive solution for accurately quantifying crack initiation, pore connection, and failure behavior of C/SiC composites.

Insights into Fracture Mechanisms and Strength Behaviors of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Elevated Temperatures

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 1800 °C in Air

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 2300 °C

Experimental Study of High-Temperature Tensile Mechanical Properties of 3D Needled C/C–SiC Composites

Analysis of the Fracture Behavior and Mechanism of PIP-C/SiC Composites at High Temperatures

An analytical model for the high temperature fracture strength of SiC fiber reinforced ceramic matrix composites considering oxidation and residual thermal stresses

High-temperature tensile behavior of 3D SiC/SiC composites

High temperature bending properties and failure mechanism of 3D needled C/SiC composites up to 2000 °C

Tensile Mechanical Behavior and Failure Mechanism of a Plain-Woven SiCf/SiC Composites at Room and Elevated Temperatures

Mechanical Properties and Microstructures of Steel-basalt Hybrid Fibers Reinforced Cement-based Composites Exposed to High Temperatures

In Situ X-ray Imaging and Numerical Modeling of Damage Accumulation in C/SiC Composites at Temperatures Up to 1200 ℃

Influence of Reinforcement with Multimodal Distribution on Thermophysical Properties and Fracture Behavior in Al-Si/SiC Composites Infiltrated under Super-Gravity Field

High-Temperature Fatigue Degradation Behaviors of a 3D Braided C/SiC with a Thin Interlayer in Different Dry Oxygen Atmospheres

Compressive Behavior of C/SiC Composites over a Wide Range of Strain Rates and Temperatures

Long‐term oxidation and ablation behavior of Cf/ZrB2–SiC composites at 1500, 2000, and 2200°C

Flexural Properties of Carbon-Carbon Composites at Temperatures Up to 2600 °C

Mechanical properties and microstructure evolution of 3D C f /SiBCN composites at elevated temperatures

Compressive experimental method and properties of C/C composites under ultra-high temperature environment

Effect of Oxidation Time on Fracture Behavior of C/SiC Composites at 800 °C in Air

Long-term oxidation and ablation behavior of C<sub>f</sub>/ZrB<sub>2</sub>-SiC composites at 1500, 2000, and 2200C

Influence of High-Temperature Oxidation and Test Conditions on the Dynamic Mechanical Properties of 2.5D SiCf/SiCm Composites