Microstructure and Corrosive-Wear Properties of CoCrFeNiZrx High Entropy Alloy Coating Fabricated on Ti6Al4V by Laser Cladding
Jiale Li,Yu Su,Jun Li,Huaqing Fu,S.W. Lee,J.G. Tang
DOI: https://doi.org/10.1016/j.jallcom.2024.177932
IF: 6.2
2024-01-01
Journal of Alloys and Compounds
Abstract:In response to the poor tribo-corrosion resistance of titanium alloys in marine engineering applications, CoCrFeNiZrx (x = 0, 0.1, 0.2, 0.3, 0.4) coatings were synthesized on Ti6Al4V substrates using laser cladding technology. The effects of Zr on phase formation, microstructure, micro-hardness, and wear resistance of CoCrFeNi coatings in diverse environments were examined. A robust metallurgical bond was established between the coating and the substrate. Through X-ray diffraction analysis and thermodynamic calculations, it was confirmed that the coating primarily consists of α-Ti and Ti2Ni phases. The introduction of Zr led to the formation of a new phase (Zr2Ni). Through scanning electron microscopy (SEM) and energy dispersive spectrometer (EDS) analysis, it is observed that with the increase in Zr content, leading to a greater infiltration of Ti from the substrate into the coatings. The grain refinement strengthening and solid solution strengthening mechanisms enhanced the micro-hardness of the coatings, which was approximately 1.6 ~ 2.1 times higher than that of the Ti6Al4V. The coatings exhibited superior wear resistance than the substrate under different environments. In dry friction conditions, the friction coefficient decreased by 16.9 ~ 55.5%, and the wear rate decreased by 14.6 ~ 33.1%, compared to the substrate. In a 3.5 weight percent (wt.%) NaCl solution at room temperature, the friction coefficient decreased by 9.5 ~ 64.5%, and the wear rate decreased by 16.5 ~ 45.1%. By integrating SEM and EDS results from the worn surfaces, the alterations in wear mechanisms of the substrate and coatings were elucidated. The study demonstrates the potential application of CoCrFeNiZrx coatings in the field of marine engineering, providing a solution to extend the service life of titanium alloys in marine environments.