Effect of Different Abrasive Particle Hardness on Erosion Resistant Performance of ZTA Structure Ceramics

鲍崇高,潘继勇

2009-01-01

Abstract:The two-phase flow of liquid and solid erosion-corrosion test was carried out to simulate different erosion-corrosion conditions. The effect of different abrasive particle hardness on the erosion-wear resistant performance of Cr15Mo3 high-Cr cast iron and ZTA structure ceramics were studied, and the erosion-wear micro-failure behavior of test materials was analyzed also. The results show that the slurry erosion volume of Cr15Mo3 high-Cr cast iron is bigger than that of ZTA ceramic on erosion-wear, and the erosion-wear resistance of ZTA ceramics is 5.8, 7.0 and 8.2 times higher than that of Cr15Mo3 high-Cr cast iron when the erosive abrasive particle is SiO2, Al2O3 and SiC, respectively. The wear amount of test materials eroded by particle with bigger hardness is also larger than that by particle with smaller hardness. It has been observed by SEM that there exists more corrosive and erosive pit morphology on the worn surface for Cr15Mo3 iron, and some of surface shows clearlyWcharacteristic for Cr15Mo3 iron, compared to smooth worn surface of ZTA ceramics. The reason for better wear resistance of ZTA is because of the finer ZrO2 grain and less pore compared with Cr15Mo3 iron.