Effect of 4 wt.% Cr on microstructure, corrosion resistance and tribological properties of Fe3Al-20 wt.%Al2O3 composites

Yaping Bai,Jiandong Xing,Shengqiang Ma,Qian Huang,Yuanyuan He,Zhen Liu,Yimin Gao

DOI: https://doi.org/10.1016/j.matchar.2013.01.014

IF: 4.537

2013-01-01

Materials Characterization

Abstract:Fe3Al–20wt.%Al2O3 ultrafine grained composites with 4wt.% Cr were prepared by mechanical alloying inducing self propagating high temperature synthesis with subsequent plasma activated sintering. Microstructures of the composites were studied by X-ray diffraction, scanning electron microscopy, energy dispersive spectrum and transmission electron microscope. Then the relative density, room temperature hardness, static corrosion resistance and dry sliding wear behavior at a temperature range of 25°C–800°C of the sintered samples were tested and analyzed. The results showed that the composites had high hardness and a good microstructure with fine grain size, high relative density. The composites with 4wt.% Cr amount also exhibited excellent comprehensive tribological properties at medium–high temperatures especially at a temperature above 500°C, although the wear resistance did not be improved at 25°C–500°C. 4wt.% Cr element addition improved the corrosion resistance of the composites significantly with the corrosion loss decreasing by 19.48%.