The alloying effects of Cr on in-situ phase evolution and wear resistance of nickel composite coatings fabricated by wide-band laser deposition
Ma Qunshuang,Chen Haozhe,Zhang Hui,Meng Wei,Hu Lei,Li Huadong,Wu Yitao,Yin Xiaohui
DOI: https://doi.org/10.1016/j.surfcoat.2020.126019
IF: 4.865
2020-09-01
Surface and Coatings Technology
Abstract:<p>In this work, nickel based composite coatings reinforced with WC and Cr particles were deposited by wide-band laser cladding. The alloying effects of Cr were investigated by microstructure characterization, phased identification, and property analysis such as microhardness and wear resistance. Results indicated the in-situ synthesized phases in laser pool mainly composed of γ-Ni solid solution, (Cr,W)<sub>5</sub>B<sub>3</sub>, (Cr,W)<sub>7</sub>C<sub>3</sub> and Cr<sub>23</sub>C<sub>6</sub>. Large quantity of block (Cr,W)<sub>5</sub>B<sub>3</sub> phases were synthesized as the Cr addition was blow 4 wt%. However, the coarse strip (Cr,W)<sub>7</sub>C<sub>3</sub> phase became the dominate precipitates as the Cr addition further increased. Statistics analysis of particle morphology showed that the (Cr,W)<sub>5</sub>B<sub>3</sub> phase was uniformly distributed block shape with median particle diameter D<sub>50</sub> = 8.97 μm, while the (Cr,W)<sub>7</sub>C<sub>3</sub> phase was coarse strip shape with median diameter D<sub>50</sub> = 12.77 μm. The average microhardness and wear resistance showed the best in coating 2# with 4 wt% Cr addition (873<sup>±85</sup>HV and 1.8 × 10<sup>−6</sup> g/m respectively). Worn surfaces indicated the strip (Cr,W)<sub>7</sub>C<sub>3</sub> phases easily peeled off and thus decreased the wear resistance of composite coatings. The results in this work showed that the constitution and content of reinforced in-situ phases in nickel composite coatings could be modified by the alloying effects of Cr. As a result, the hardness and wear resistance were also improved with optimized Cr addition.</p>
physics, applied,materials science, coatings & films