Manipulation of Magnetic Properties and Magnetoresistance in Co/Cu/γ′-Fe4N/Mica Flexible Spin Valves Via External Mechanical Strains

Xia Chen,Xiaohui Shi,Zeyu Zhang,Xiang Liu,Chao Jin,Wenbo Mi

DOI: https://doi.org/10.1021/acsaelm.1c00999

IF: 4.494

2022-01-01

ACS Applied Electronic Materials

Abstract:The strain-tailored magnetic and electronic transport properties in flexible spin valves (SPVs) have attracted attention due to their practical applications in flexible spintronic devices. Here, magnetic and spin-dependent electronic transport properties of Co/Cu/gamma'-Fe4N/mica flexible SPVs are investigated. The strain-induced change ratio of magnetoresistance (MR) is 49% in Co(4.8 nm)/Cu(7.5 nm)/gamma'-Fe4N(11.0 nm) flexible SPVs. The magnetic properties of Co(4.8 nm)/Cu(7.5 nm)/gamma'-Fe4N(7.9 nm) flexible SPVs show mechanical stability at bending strains. The magnetic properties of flexible SPVs did not deteriorate after 100 times of bending and 60 h of bending. As the Co layer thickness decreases from 7.2 to 2.4 nm, the sign of MR changes from negative to positive. A negative MR appears due to the opposite scattering spin asymmetry coefficients between Co/Cu and gamma'-Fe4N/Cu interfaces. A positive MR arises from the same scattering spin asymmetry coefficients at Co/Cu and gamma'-Fe4N/Cu interfaces or magnetization misalignments between Co and gamma'-Fe4N layers. Additionally, the MR is a combination of an anisotropy magnetoresistance and a giant magnetoresistance effect, which has been confirmed by MR-H curves with different measurement configurations (Hin-plane parallel to I, Hin-plane perpendicular to I and Hout-of-plane perpendicular to I) and M-H curves. The M-H curves show that the magnetization of gamma'-Fe4N reverses before that of the Co layer.