Manipulation of Magnetic Properties and Magnetoresistance in Co/Cu/γ′-Fe 4 N/Mica Flexible Spin Valves via External Mechanical Strains

Xia Chen,Xiaohui Shi,Zeyu Zhang,Xiang Liu,Chao Jin,Wenbo Mi

DOI: https://doi.org/10.1021/acsaelm.1c00999

IF: 4.494

2022-01-11

ACS Applied Electronic Materials

Abstract:The strain-tailored magnetic and electronic transport properties in flexible spin valves (SPVs) have attracted attention due to their practical applications in flexible spintronic devices. Here, magnetic and spin-dependent electronic transport properties of Co/Cu/γ′-Fe4N/mica flexible SPVs are investigated. The strain-induced change ratio of magnetoresistance (MR) is 49% in Co­(4.8 nm)/Cu­(7.5 nm)/γ′-Fe4N­(11.0 nm) flexible SPVs. The magnetic properties of Co­(4.8 nm)/Cu­(7.5 nm)/γ′-Fe4N­(7.9 nm) flexible SPVs show mechanical stability at bending strains. The magnetic properties of flexible SPVs did not deteriorate after 100 times of bending and 60 h of bending. As the Co layer thickness decreases from 7.2 to 2.4 nm, the sign of MR changes from negative to positive. A negative MR appears due to the opposite scattering spin asymmetry coefficients between Co/Cu and γ′-Fe4N/Cu interfaces. A positive MR arises from the same scattering spin asymmetry coefficients at Co/Cu and γ′-Fe4N/Cu interfaces or magnetization misalignments between Co and γ′-Fe4N layers. Additionally, the MR is a combination of an anisotropy magnetoresistance and a giant magnetoresistance effect, which has been confirmed by MR–H curves with different measurement configurations (H in‑plane∥I, H in‑plane⊥I and H out‑of‑plane⊥I) and M–H curves. The M–H curves show that the magnetization of γ′-Fe4N reverses before that of the Co layer.

materials science, multidisciplinary,engineering, electrical & electronic