Abstract:The formation mechanism of α″-Fe16N2 phase was investigated in the form of nanoparticles. Both α-Fe and γ-Fe2O3 nanoparticles were used to prepare α″-Fe16N2 by using a low-temperature nitriding process (≤180 °C). The synthesized α″-Fe16N2 nanoparticles have a high α″-Fe16N2 volume ratio up to 93%, with a specific saturation magnetization of 178 emu/g (room temperature) and coercivity of 2.0 kOe. The formation of α″-Fe16N2 phase includes three stages: (1) the heterogenous nucleation of α″-Fe16N2 with simultaneous chemical reaction, (2) the growth of α″-Fe16N2 with a local electric field in the Fe16N2 layer, and (3) the termination of Fe16N2 growth due to the nucleation of other Fe–N phases (ε-Fe3N or γ′-Fe4N). In low-temperature nitriding, NH3 was used as the nitrogen source. The adsorbed NH3 molecules on the Fe surface decompose into N and H atoms, and then N atoms react with Fe and nucleation of α″-Fe16N2 simultaneously occurs at the high-energy surface sites of reduced Fe nanoparticles. The growth of α″-Fe16N2 phase can be explained by the electric field modified diffusion theory, where the electric field is established by the migration of Fe and N ions and electrons. Finally, the nucleation of Fe–N stable phases (ε-Fe3N or γ′-Fe4N) ceases the further growth of α′′-Fe16N2 layer. Then, there is critical thickness for the α″-Fe16N2 layer, which is estimated to be 10–15 nm from the surface. Therefore, single-phase α″-Fe16N2 nanoparticles are expected in fine particles with less than 30 nm in diameter.

Synthesis of α′′-Fe16N2 ribbons with a porous structure

Synthesis Of A 00 - Fe16n2 Ribbons With A Porous Structure

Synthesis of α′′-Fe<sub>16</sub>N<sub>2</sub>ribbons with a porous structure

Formation of Nanocrystalline Fe–N–B–Cu Soft Magnetic Ribbons

Crystallization kinetics and magnetic properties of Fe 63.5Co10Si13.5B9Cu 1Nb3 nanocrystalline powder cores

Nanocrystalline Soft Magnetic Ribbon with Α″-Fe16n2 Nanocrystallites Embedded in Amorphous Matrix

Synthesis of α”-Fe16N2 foils with an ultralow temperature coefficient of coercivity for rare-earth-free magnets

Influence of Fabrication Process on Magnetic Properties of Co-Finemet Nanocrystalline Powder Core

Crystallization Kinetics and Magnetic Properties of Fe73.5si13.5b9cu1nb1v2 Nanocrystalline Powder Cores

Crystallization Kinetics of Co-Finemet Amorphous Alloys and Magnetic Properties of Nanocrystalline Powder Cores

Critical Thickness of Α″-Fe16n2 Layer Prepared in Low-Temperature Nitriding

Preparation of Α′-Fe(n)/α′-fe8n by Γ′-Fe4n Precursor

Preparation of Fe–Ni–P–B Metallic Nano-Ribbons

Nanocrystalline Fe83Si4B10P2Cu1 ribbons with improved soft magnetic properties and bendability prepared via rapid annealing of the amorphous precursor

Fabrication of Fe-6.5wt%Si Ribbons by Melt Spinning Method on Large Scale

Influence of Low-Temperature Nitridation on Low-Frequency Magnetization of Fe82nb7b10cu1 Nanocrystalline Alloy Ribbons

Structure, thermodynamic behavior and static magnetic properties of Al addition FeCoNbCuB alloy ribbons

Crystallization Process of Nanocrystalline (FeCo)(78)Nb6B15Cu1 Alloy and Its Magnetic Characterization

On the Effect of the Melt Cooling Rate upon Spinning on the Structure of the Surface Layers of Fe77Ni1Si9B13 Alloy Ribbons

Structure and Properties of a Ribbon from FeCoNiSiB High-Entropy Alloy

High Coercivity Nd-Ce-Fe-B Nanostructured Ribbons Prepared from Melt Spinning Technique