The Promotional Effect of Copper in Catalytic Oxidation by Cu-Doped α-MnO2 Nanorods

Xiaolei Hu,Junxiao Chen,Shuya Li,Yaxin Chen,Weiye Qu,Zhen Ma,Xingfu Tang

DOI: https://doi.org/10.1021/acs.jpcc.9b09891

2020-01-01

Abstract:α-MnO2 has broad applications in catalytic oxidation. Its catalytic performance may be further improved by doping α-MnO2 with a metal ion, such as the Cu ion, but the reasons for the promoting effe...

What problem does this paper attempt to address?

Remarkable Synergy Effect of Cu–Nb Oxide Nanorods Toward Electrocatalytic Nitrogen Reduction: the Enhanced Mass and Electron Transfer

Shuyue Wang,Chao Qian,Xinzhi Chen,Shaodong Zhou

DOI: https://doi.org/10.1021/acscatal.4c01203

IF: 12.9

2024-01-01

ACS Catalysis

Abstract:The modification of Nb2O5 materials toward an enhanced nitrogen reduction process is reported. The Lewis acidic Nb-O site is identified as the most promising electrocatalytic activity of all Nb-X structures considered. To facilitate both mass and electron transfer, thus further enhancing the electrocatalytic hydrogenation of dinitrogen on the Nb2O5 surface, selective doping and the morphology optimization were employed to regulate the electronic structure. Experiments point out the appropriate size and shape of Nb2O5 materials in nitrogen hydrogenation, while theoretical screening reveals the doping effect of Cu on promoting electron transfer by eliminating the bandgap. The high-performance Cu-doped Nb2O5 species is thus afforded.
Copper Doped Manganese Oxides to Produce Enhanced Catalytic Performance for CO Oxidation

Xiaoran Niu,Zuotao Lei

DOI: https://doi.org/10.1016/j.jece.2019.103055

IF: 7.7

2019-01-01

Journal of Environmental Chemical Engineering

Abstract:The copper species doped into manganese oxides have a positive influence on the catalytic performance. In this paper, Cu-doped Mn3O4nanoparticles and Cu-doped Mn2O3hollow nanospheres were controllably synthesized through a one-step facile, green solvothermal strategy and characterized by XRD, BET-BJH, TEM, FE-SEM, EDS, Raman, XPS and TPR analyses. The formation of Cu-doped Mn3O4and Cu-doped Mn2O3phases can be ingeniously controlled by adjusting H2O2content and the mechanism of crystal growth was studied based on time-dependent experiments. The catalytic CO oxidation results showed that the temperature corresponding to 50% of the CO conversion (T50) was about 162 °C and 223 °C for Cu-doped Mn2O3 and Cu-doped Mn3O4, which was 63 °C and 22 °C lower than pure Mn2O3and Mn3O4, demonstrating that the Cu-doped MnOxnanoparticles exhibit enhanced catalytic capacity for CO oxidation. Also, the stability and reusability of Cu-doped MnOxwere investigated and the results indicate high reusability and stability of the catalyst.
Doping effect of transition metals (Zr, Mn, Ti and Ni) on well-shaped CuO/CeO 2 (rods): nano/micro structure and catalytic performance for selective oxidation of CO in excess H 2 .

Xiaolin Guo,Zhihuan Qiu,Jianxin Mao,Renxian Zhou

DOI: https://doi.org/10.1039/c8cp03696a

IF: 3.3

2018-01-01

Physical Chemistry Chemical Physics

Abstract:A series of CuO/CeM(rod) catalysts doped by transition metals were prepared and systematically characterized. The introduction of Mn and Ti plays a significant role in promoting the catalytic performance of the CuO/CeO2(rod) catalyst for the preferential oxidation of CO in H-2-rich gas, while the doping with Zr basically maintains the same catalytic activity and Ni leads to a negative influence. Mn and Ti additives remarkably enrich the formation of defect structures and promote copper ion incorporation into the surface of CeM(rod), which greatly facilitates the generation of strong interfacial copper-ceria interaction in CuO/CeMn(rod) and CuO/CeTi(rod). In addition, CuO/CeMn(rod) possesses excellent surface oxygen mobility at low temperature due to the existence of manganese species with multiple valence states and todorokite species. The Ce-doped perovskite structure (Na0.5Ce0.5TiO3) further adjusts the oxygen vacancy in CuO/CeTi(rod) and anchors copper oxide species with strong interactions. Although a homogeneous solid solution is formed in CeZr(rod) with increased amounts of oxygen vacancies, the interaction between copper and ceria species in the interface of CuO/CeZr(rod) remains the same as with CuO/CeO2(rod). The addition of Ni impairs the dispersion of copper oxide and weakens the copper-ceria interaction, which damages the catalytic performance of CuO/CeNi(rod).
Transition Metal (fe2o3, Co3O4 and NiO)-Promoted CuO-Based Α-Mno2 Nanowire Catalysts for Low-Temperature CO Oxidation

Haiou Zhang,Yixin Zhang,Huikang Song,Yan Cui,Yingying Xue,Cai-e Wu,Chao Pan,Jingxin Xu,Jian Qiu,Leilei Xu,Mindong Chen

DOI: https://doi.org/10.3390/catal13030588

IF: 3.9

2023-01-01

Catalysts

Abstract:As a toxic pollutant, carbon monoxide (CO) usually causes harmful effects on human health. Therefore, the thermally catalytic oxidation of CO has received extensive attention in recent years. The CuO-based catalysts have been widely investigated due to their availability. In this study, a series of transition metal oxides (Fe2O3, Co3O4 and NiO) promoted CuO-based catalysts supported on the α-MnO2 nanowire catalysts were prepared by the deposition precipitation method for catalytic CO oxidation reactions. The effects of the loaded transition metal type, the loading amount, and the calcination temperature on the catalytic performances were systematically investigated. Further catalyst characterization showed that the CuO/α-MnO2 catalyst modified with 3 wt% Co3O4 and calcined at 400 °C performed the highest CO catalytic activity (T90 = 75 °C) among the investigated catalysts. It was supposed that the loading of the Co3O4 dopant not only increased the content of oxygen vacancies in the catalyst but also increased the specific surface area and pore volume of the CuO/α-MnO2 nanowire catalyst, which would further enhance the catalytic activity. The CuO/α-MnO2 catalyst modified with 3 wt% NiO and calcined at 400 °C exhibited the highest surface adsorbed oxygen content and the best normalized reaction rate, but the specific surface area limited its activity. Therefore, the appropriate loading of the Co3O4 modifier could greatly enhance the activity of CuO/α-MnO2. This research could provide a reference method for constructing efficient low-temperature CO oxidation catalysts.
Promotional Effects of Cu O on the Activity of Cu/ZnO Catalyst Toward Efficient CO Oxidation

Bismark Sarkodie,Yanjie Hu,Wei Bi,Jiechao Jiang,Chunzhong Li

DOI: https://doi.org/10.1016/j.apsusc.2021.149241

IF: 6.7

2021-01-01

Applied Surface Science

Abstract:Tailoring the configuration at metal and support interface contributes to an effective pathway for fabricating catalysts of high catalytic performance for scientific and industrial applications. In this study, the CO oxidation activity over spray-pyrolyzed copper doped Zinc oxide (Cu/ZnO) catalyst was enhanced by deposition-precipitation of 1 wt% Copper (CuxO-Cu/ZnO). Copper ions substituted into ZnO caused defects which altered the physiochemical properties of the catalyst and acted as a bridge to accelerate the transfer of charge carriers to the surface, but the promoting effect of CuxO incorporated by deposition-precipitation elevated the catalytic performance of the catalyst. The activation energy of CuxO-Cu/ZnO (24.52 KJ mol(-1)) was extremely lower than that of 20 wt% Cu/ZnO (32.19 KJ mol(-1)) catalyst in CO oxidation due to the active and populous Cu (I) species in CuxO-Cu/ZnO. Defects created by the incorporation of Cu species in CuxO-Cu/ZnO catalyst contributed to low-temperature reducibility, oxygen mobility and abundant oxygen vacancies, which played fundamental role in enhancing the activity of CuxO-Cu/ZnO, compared its counterpart. The critical role of the active Cu+ sites was further confirmed by In-situ DRIFTS.
Single-ion Copper Doping Greatly Enhances Catalytic Activity of Manganese Oxides Via Electronic Interactions.

Xiaolei Hu,Shuya Li,Yaxin Chen,Weiye Qu,Junxiao Chen,Zhen Ma,Xingfu Tang

DOI: https://doi.org/10.1039/c9cc07669g

IF: 4.9

2020-01-01

Chemical Communications

Abstract:Single-ion copper doping greatly enhances catalytic activity of manganese oxides via electronic interactions between copper ions and manganese ions.
Enhancing the Low-Temperature CO Oxidation over CuO-Based -MnO2 Nanowire Catalysts

Yan Cui,Huikang Song,Yiyu Shi,Pengxiang Ge,Mindong Chen,Leilei Xu

DOI: https://doi.org/10.3390/nano12122083

2022-01-01

Abstract:A series of CuO-based catalysts supported on the alpha-MnO2 nanowire were facilely synthesized and employed as the CO oxidation catalysts. The achieved catalysts were systematically characterized by XRD, SEM, EDS-mapping, XPS and H-2-TPR. The catalytic performances toward CO oxidation had been carefully evaluated over these CuO-based catalysts. The effects of different loading methods, calcination temperatures and CuO loading on the low temperature catalytic activity of the catalyst were investigated and compared with the traditional commercial MnO2 catalyst with a block structure. It was found that the slenderness ratio of a CuO/alpha-MnO2 nanowire catalyst decreases with the increase in CuO loading capacity. The results showed that when CuO loading was 3 wt%, calcination temperature was 200 degrees C and the catalyst that was supported by the deposition precipitation method had the highest catalytic activity. Besides, the alpha-MnO2 nanowire-supported catalysts with excellent redox properties displayed much better catalytic performances than the commercial MnO2-supported catalyst. In conclusion, the CuO-based catalysts that are supported by alpha-MnO2 nanowires are considered as a series of promising CO oxidation catalysts.
Enhancing CO catalytic oxidation performance over Cu-doping manganese oxide octahedral molecular sieves catalyst

Chao Jin,Wenzhe Si,Ya Chen,Xiaoguang Zhao,Bin Zhou,Yu Shen,Qiangqiang Zhu,Yang Chu,Feng Liu,Mingfeng Li,Junhua Li

DOI: https://doi.org/10.1016/j.jcis.2024.02.051

IF: 9.9

2024-03-01

Journal of Colloid and Interface Science

Abstract:The CO oxidation catalytic activity of catalysts is strongly influenced by the oxygen vacancy defects (OVDs) concentration and the valence state of active metal. Herein, a defect engineering approach was implemented to enhance the oxygen vacancy defects and to modify the valence of metal ions in manganese oxide octahedral molecular sieves (OMS-2) by the introduction of copper (Cu). The characterization and theoretical calculation results reveal that the incorporation of Cu 2+ ion into the OMS-2 structure led to a rise in specific surface area and pore volume, weakening of Mn-O bonds, higher proportion of the low-coordinated oxygen species adsorbed in oxygen vacancies (O ads ) and an increase in the average oxidation state of manganese. These structural modifications were discovered to considerably reduce the apparent activation energy (Ea), thus ultimately significantly enhancing the CO oxidation activity (T 99 at 148 °Cat GHSV = 13,200 h −1 ) than the original OMS-2 (T 99 = 215 °C at GHSV = 13,200 h −1 ). Furthermore, In-situ diffuse reflectance infrared Fourier transform (DRIFT) and In-situ near-ambient pressure X-ray photoelectron spectroscopy (in situ NAP-XPS) results indicate that the bimetallic synergy enhanced by doping strategy accelerates the conversion of oxygen to chemisorbed oxygen species and the reaction rate of CO oxidation through Mn 3+ +Cu 2+ ↔Mn 4+ +Cu + redox cycle. The findings of this study offer novel perspectives on the design of catalysts with exceptional performance in CO oxidation.

chemistry, physical
Promotional effect for SCR of NO with CO over MnO -doped Fe3O4 nanoparticles derived from metal-organic frameworks

Yu Zhang,Ling Zhao,Ziang Chen,Xinyong Li

DOI: https://doi.org/10.1016/j.cjche.2021.03.043

IF: 3.8

2021-06-01

Chinese Journal of Chemical Engineering

Abstract:MnO x -Fe3O4 nanomaterials were fabricated by using the innovative scheme of pyrolyzing manganese-doped iron-based metal organic framework in inert atmosphere and exhibited extraordinary performance of NO reduction by CO (CO-SCR). Multi-technology characterizations were conducted to ascertain the properties of fabricated materials (e.g., TGA, XRD, SEM, FT-IR, XPS, BET, H2-TPR and O2-TPD). Moreover, the interaction between reactants and catalysts was ascertained by in situ FT-IR. Experimental results demonstrated that Mn was an ideal promoter for iron oxides, resulting in decrease of crystallite size, improve reducibility property, enhance the mobility and the amount of lattice O2− species, as well as strength the adsorption ability of active NO and CO to form multiple species (e.g., nitrate and carbonate). The unprecedented enhancement of CO-SCR activity over Mn-Fe nanomaterials follows the Eley-Rideal (E-R) and Langmuir-Hinshelwood (L-H) reaction pathway.

engineering, chemical
Copper Manganese Oxides Supported on Multi-Walled Carbon Nanotubes As an Efficient Catalyst for Low Temperature CO Oxidation

Yafei Guo,Jin Lin,Changhai Li,Shouxiang Lu,Chuanwen Zhao

DOI: https://doi.org/10.1007/s10562-016-1869-4

IF: 2.936

2016-01-01

Catalysis Letters

Abstract:Multi-walled carbon nanotubes (MWCNTs) with unique properties are finding increasing utility in catalytic applications. In this work, Cu–Mn@MWCNTs (copper manganese oxides supported on MWCNTs) was synthesized as an efficient catalyst for low temperature CO oxidation. The catalyst was characterized by N2 adsorption–desorption, field emission scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction, Fourier transform infrared spectroscopy, and X-ray photoelectron spectroscopy. The CO oxidation activity and long-term working stability of the catalyst were evaluated in 0.1–0.5 % CO and balanced air using a modified fixed-bed reactor. The effects of CO concentration and Cu/Mn molar ratio on the CO oxidation performances were also demonstrated. The increasing CO concentration (0.1–0.5 %) will impair the CO oxidation performances due to the covering of active sites and formation of carbonates and/or hydroxyl species. The increased CO oxidation activity with the changing Cu/Mn molar ratio (1:8–1:1) is ascribed to the improving oxygen utilization in the redox process by increasing Cu content. The synergistic interaction within the Cu–Mn bimetallic catalytic system and the unique properties of the MWCNTs support are also highlighted for the enhanced CO oxidation activity. The catalyst could be considered as a promising option for removing trace CO from typical confined spaces such as space-crafts, submarines and mine refuge chambers.
Low-Temperature Catalytic Oxidation of Volatile Organic Compounds (VOCs) using Transition Metal Mixed Oxide Catalysts

Khắc Tuấn Nguyễn,Duong Hoang Anh,Ta Dinh Quang,Minh THắng Lê

DOI: https://doi.org/10.62239/jca.2024.041

2024-06-30

Vietnam Journal of Catalysis and Adsorption

Abstract:This paper discusses the modification of MnOx by doping various metals, such as Cu, supported on cordierite honeycomb ceramics, which were easily synthesized by using the impregnation method. The physicochemical properties were comprehensively featured via the BET, XRD, SEM-EDX and H2-TPR techniques. Activity results suggested that the introduction of doping metals significantly enhanced the catalytic performance of Cu1Mn2Ox compared to single metal oxides. Furthermore, in the catalytic oxidation of benzene and toluene, the monolithic Cu1Mn2Ox catalyst demonstrates the best catalytic performance. It was able to completely oxidize the two compounds at 275oC with a reaction velocity (WHSV) of about 18,000 mL/(g•hr) and pollutant concentrations of 7000 ppm and 12000 ppm, respectively. The formation of a Cu-Mn solid solution with spinel Cooper-Manganese structure was thought to be the cause of the excellent catalytic performance of monolithic Cu1Mn2Ox. This resulted in an increase in the amount of adsorbed oxygen species on the surface and a high lattice oxygen mobility. This can improve catalyst reducibility and oxygen species activity, as demonstrated by significantly higher dehydrogenation temperatures of Cu-Mn composite oxides through H2-TPR. Meanwhile, the monolithic Cu1Mn2Ox catalyst showed good stability in 16 hours of testing and cycle ability test and showed great potential in practical application.
The Promotion Effect of Manganese on Cu/SAPO for Selective Catalytic Reduction of NOx with NH3

Chengkai Pang,Yuqun Zhuo,Qiyu Weng,Zhenwu Zhu

DOI: https://doi.org/10.1039/c7ra12350g

IF: 4.036

2018-01-01

RSC Advances

Abstract:The activity and hydrothermal stability of Cu/SAPO and xMn-2Cu/SAPO for low-temperature selective catalytic reduction of NO x with ammonia were investigated. An ion-exchanged method was employed to synthesize xMn-2Cu/SAPO, which was characterized by N2 adsorption, ICP-AES, X-ray diffraction (XRD), NH3-temperature programmed desorption (NH3-TPD), NO oxidation, X-ray photoelectron spectrum (XPS), UV-vis, H2-temperature programmed reduction (H2-TPR) and diffuse reflectance infrared Fourier transform spectra (DRIFTS). 2Mn-2Cu/SAPO and 4Mn-2Cu/SAPO showed the best SCR activity, in that at 150 °C NO conversion reached 76% and N2 selectivity was above 95% for the samples. NO oxidation results showed that the 2Mn-2Cu/SAPO had the best NO oxidation activity and the BET surface area decreased as manganese loading increased. XRD results showed that the metal species was well dispersed. NH3-TPD showed that the acid sites have no significant influence on the SCR activity of xMn-2Cu/SAPO. H2-TPR patterns showed good redox capacity for xMn-2Cu/SAPO. UV-vis and H2-TPR showed that the ratio of Mn4+ to Mn3+ increased as manganese loading increased. XPS spectra showed a significant amount of Mn3+ and Mn4+ species on the surface and addition of manganese increased the ratio of Cu2+. The promotion effect of manganese to 2Cu/SAPO comes from the generation of Mn3+ and Mn4+ species. Deduced from the DRIFTS spectra, the Elay-Rideal mechanism was effective on 4Mn-2Cu/SAPO.
Hetero-metal Cation Control of CuO Nanostructures and Their High Catalytic Performance for CO Oxidation.

Hongwen Huang,Liqiang Zhang,Kewei Wu,Qing Yu,Ru Chen,Hangsheng Yang,Xinsheng Peng,Zhizhen Ye

DOI: https://doi.org/10.1039/c2nr32729e

IF: 6.7

2012-01-01

Nanoscale

Abstract:A controllable synthesis of various morphologies of CuO nanostructures with tuning by hetero-metal cations has been developed in aqueous solution at room temperature. The morphologies of CuO can be engineered from nanosheets to nanoparticles with different length ratios of the long axis to the short axis. The formation of many metal-ion complexes plays an important role in slowing the release rate of OH- and affects the reaction kinetics further. We found that the effect of hetero-metal cations on the final morphology of the CuO nanostructures was the same as that of the cooling temperature. A series of temperature-controlled experiments demonstrated this. Furthermore, among all the synthesized CuO nanostructures, the fascinating colloidal mesoporous CuO quasi-monocrystalline nanosheets prepared at 25 degrees C with a thickness of ca. 10 nm and large specific surface area of 80.32 m(2) g(-1) is investigated intensively. These CuO nanosheets demonstrate a superior catalytic activity for CO oxidation, with features of high CO conversion efficiency (47.77 mmol(CO) g(CuO)(-1) h(-1) at 200 degrees C), which is close to that reported for previously investigated supported-CuO catalysts, and a low apparent activation energy E-a (53.3 kJ mol(-1)).
Effects of different manganese precursors as promoters on catalytic performance of CuO-MnOx/TiO2 catalysts for NO removal by CO.

Chuanzhi Sun,Yingjie Tang,Fei Gao,Jingfang Sun,Kaili Ma,Changjin Tang,Lin Dong

DOI: https://doi.org/10.1039/c5cp02158h

IF: 3.3

2015-01-01

Physical Chemistry Chemical Physics

Abstract:Two different precursors, manganese nitrate (MN) and manganese acetate (MA), were employed to prepare two series of catalysts, i.e., xCuyMn(N)/TiO2 and xCuyMn(A)/TiO2, by a co-impregnation method. The catalysts were characterized by XRD, LRS, CO-TPR, XPS and EPR spectroscopy. The results suggest that: (1) both xCuyMn(N)/TiO2 and xCuyMn(A)/TiO2 catalysts exhibit much higher catalytic activities than an unmodified Cu/TiO2 catalyst in the NO + CO reaction. Furthermore, the activities of catalysts modified with the same amount of manganese are closely dependent on manganese precursors. (2) The enhancement of activities for Mn-modified catalysts should be attributed to the formation of the surface synergetic oxygen vacancy (SSOV) Cu+-square-Mny+ in the reaction process. Moreover, since the formation of the SSOV (Cu+-square-Mn-3(+)) in the xCuyMn(N)/TiO2 catalyst is easier than that (Cu+-square-Mn2+) in the xCuyMn(A)/TiO2 catalyst, the activity of the xCuyMn(N)/TiO2 catalyst is higher than that of the xCuyMn(A)/TiO2 catalyst. This conclusion is well supported by the XPS and EPR results.
Preparation,Characterization and Catalytic Performance of CuO/Mn_2O_3/γ-Al_2O_3 Catalysts over CO Oxidation

DAI Yue,LI Shan-Shan,TANG Chang-Jin,YAO Xiao-Jiang,QI Lei,LIU Bin,GAO Fei,DONG Lin

2012-01-01

Chinese journal of inorganic chemistry

Abstract:A series CuO/Mn2O3/γ-Al2O3 catalysts were prepared by impregnation and characterized by XRF,XRD,H2-TPR,in-situ FT-IR and activity test for oxidation of carbon monoxide.The model reaction of CO+O2 tests showed that,modification of γ-Al2O3 by Mn2O3 promoted activities of CuO/γ-Al2O3 catalysts.XRD results proved that the amount of well-dispersed Cu2+ species was increased after the modification by Mn2O3,and it was also found that the catalytic activities were not only decided by the amount of well-dispersed Cu2+ species.Furthermore,TPR and in-situ FT-IR results revealed that the activities of catalysts were in good line with the reducibility of well-dispersed copper and manganese oxides species.
One-Step Synthesis of Nanostructured Cu–Mn/TiO 2 via Flame Spray Pyrolysis: Application to Catalytic Combustion of CO and CH 4

Xing Yuan,Menglei Qing,Lingquan Meng,Haibo Zhao

DOI: https://doi.org/10.1021/acs.energyfuels.0c02747

2020-11-03

Abstract:Catalytic combustion has been widely applied to remove the trace combustible pollutants. However, the earth-abundant and high-performance nanocatalysts are still the main research focus on promoting catalytic efficiency. Herein, the Cu and Mn mixed oxides supported on TiO2 nanoparticles with various Cu and Mn molar contents synthesized via the flame spray pyrolysis (FSP) technique are utilized in the catalytic oxidation of lean CO and CH4. Initially, the Cu–Mn/TiO2 nanocatalysts are composed of spherical structures with a diameter of about 20 nm, whose specific surface area is between 60 and 90 m2/g. The Cu element is more evenly distributed on the TiO2 surface than the Mn element, owing to the distinctly different ion radii. Both the copper and manganese cations could incorporate into the TiO2 lattice, which generates oxygen vacancies and enhances the diffusion of oxygen ions, causing the transformation of the antanse to rutile phase. When the molar content of the Cu–Mn increases to less than 30 mol %, the temperature of its reduction peak keeps decreasing due to the hydrogen spillover effect. Moreover, the catalytic performances of the Cu–Mn/TiO2 with 12 mol % loading (12CMT) are all optimal during the low-temperature and the high-temperature stages, which are superior to the FSP-made copper manganese or copper titanium oxides. This is attributed to the small crystal particles, highly dispersed active components of CuOx and MnOx, and the higher ratios of Cu1+/Cu and Mn4+–Oads Lewis acid–base pairs. In addition, the strong interaction between Cu–Mn components and rutile phase support can tremendously promote the activity of catalytic combustion. Under the simulated flue gas, the catalytic properties of 12CMT decreases in comparison with those of CO and CH4 mixed gas due to the introduction of CO2. Ultimately, the Cu–Mn/TiO2 samples exhibit the outstanding water resistance, thanks to the hydrophobization of the catalyst surface.This article has not yet been cited by other publications.

energy & fuels,engineering, chemical
The promotion effect of manganese on Cu/SAPO for selective catalytic reduction of NOx with NH3

Chengkai Pang,Yuqun Zhuo,Qiyu Weng,Zhenwu Zhu

DOI: https://doi.org/10.1039/c7ra12350g

IF: 4.036

2018-01-01

RSC Advances

Abstract:The activity and N2 selectivity of Cu/SAPO and xMn–2Cu/SAPO for low-temperature selective catalytic reduction of NOx with NH3 were investigated.
Revealing the intrinsic nature of Cu- and Ce-doped Mn3O4 catalysts with positive and negative effects on CO oxidation using operando DRIFTS-MS

Zihao Hu,Xiaoying Zhou,Tiantian Zhang,Zuliang Wu,Jing Li,Wei Wang,Erhao Gao,Jiali Zhu,Shuiliang Yao

DOI: https://doi.org/10.1039/d4dt02391a

2024-10-22

Abstract:Aiming at the problem of the poor performance of an Mn-MOF-74-derived Mn3O4 catalyst in low-temperature carbon monoxide (CO) oxidation, copper (Cu) and cerium (Ce) elements were used to modify the Mn3O4 catalyst to improve its performance in low-temperature CO oxidation. According to the results of catalytic performance testing, the CO oxidation activity of the Cu0.3Mn2.7O4 catalyst was significantly improved compared with that of the pristine Mn3O4 catalyst, when a CO conversion rate of 90% was achieved at 118 °C. According to X-ray photoelectron spectroscopy and Brunauer-Emmett-Teller analyses, the (Mn2+ + Mn3+)/(Mn2+ + Mn3+ + Mn4+) ratio and the Oads/Ototal ratio increased after Cu doping, indicating promoted oxygen vacancy generation. In addition, the increased specific surface area was beneficial for the adsorption of reactant molecules and the exposure of active sites. According to H2-temperature-programmed reduction characterization, Cu doping significantly enhanced the performance of the Cu0.3Mn2.7O4 catalyst during low-temperature redox. Finally, these factors synergistically promoted the degradation of CO over the Cu0.3Mn2.7O4 catalyst. In addition, operando diffuse reflectance Fourier transform infrared spectroscopy results suggested the presence of more terminal-type oxygen, which is essential for the catalytic oxidation of CO on the surface of the Cu0.3Mn2.7O4 catalyst. Moreover, the Cu0.3Mn2.7O4 catalyst also showed excellent resistance to carbonate, and remarkable stability.
Manganese Doping in Cobalt Oxide Nanorods Promotes Catalytic Dehydrogenation

Qingping Ke,Ding Yi,Yangxin Jin,Fei Lu,Bo Zhou,Fei Zhan,Yijun Yang,Denglei Gao,Pengfei Yan,Chao Wan,Ping Cui,Dmitri Golberg,Jiannian Yao,Xi Wang

DOI: https://doi.org/10.1021/acssuschemeng.0c00842

IF: 8.4

2020-01-01

ACS Sustainable Chemistry & Engineering

Abstract:Heteroatom doping in nanomaterials can import new active sites and promote catalytic activity. Here we report that Mn-doped Co3O4 nanorods (Mn-x-Co3O4) via substituting Mn3+- (t(2g)(3)-e(g)(1)) for Co3+ (t(2g)(6)-e(g)(0)) exhibit similar to 100% yield for 4-methyl benzyl alcohol dehydrogenation catalysis at 60 degrees C and no decay (8 cycles), compared with only 1.4% of activity for bare Co(3)O(4 )catalysts. We characterize the fine structures of Mn-x-Co3O4 at the atomic level and demonstrate that the superior catalytic performance is strongly related to the Mn3+-induced Jahn-Teller (J-T) effect, which is a geometric distortion that has generally been considered to be disadvantageous for applications. Experimental observations and theoretical calculations reveal that unsaturated Mn3+ with J-T distortion acts as an active site, and readily reacts with -OH groups of benzyl alcohol adsorbed nearby, simultaneously promoting dehydrogenation to directly yield benzaldehyde. Mn-x-Co3O4 catalysts rapidly dehydrogenate alcohols into aldehydes/ketones for 19 reactions with >99.9% selectivity and 14 examples with >90.2% yield.
Surface structure effects in nanocrystal MnO2 and Ag/MnO2 catalytic oxidation of CO

Run Xu,Xun Wang,Dingsheng Wang,Kebin Zhou,Yadong Li,R XU,X WANG,D WANG,K ZHOU,Y LI

DOI: https://doi.org/10.1016/j.jcat.2005.10.026

IF: 7.3

2006-01-25

Journal of Catalysis

Abstract:Pure-phase α-MnO2 and β-MnO2 nanowires/nanorods were synthesized through an easy solution-based hydrothermal method, and the effect of the manganese dioxide phase on the activity of MnO2 and Ag/MnO2 for the oxidation of CO was investigated. MnO2 is an effective catalyst in CO oxidation, and its activity depends on the crystal phase of MnO2. α-MnO2 exhibits a higher activity than β-MnO2, because the α-MnO2 nanowires can be reduced more easily than the β-MnO2 nanorods. Moreover, when Ag was introduced to MnO2, a strong interaction occurred between Ag and MnO2. The catalytic activity clearly correlates with this interaction, which is determined by crystal phase and surface structure.

chemistry, physical,engineering, chemical

The Promotional Effect of Copper in Catalytic Oxidation by Cu-Doped α-MnO2 Nanorods

Remarkable Synergy Effect of Cu–Nb Oxide Nanorods Toward Electrocatalytic Nitrogen Reduction: the Enhanced Mass and Electron Transfer

Copper Doped Manganese Oxides to Produce Enhanced Catalytic Performance for CO Oxidation

Doping effect of transition metals (Zr, Mn, Ti and Ni) on well-shaped CuO/CeO 2 (rods): nano/micro structure and catalytic performance for selective oxidation of CO in excess H 2 .

Transition Metal (fe2o3, Co3O4 and NiO)-Promoted CuO-Based Α-Mno2 Nanowire Catalysts for Low-Temperature CO Oxidation

Promotional Effects of Cu O on the Activity of Cu/ZnO Catalyst Toward Efficient CO Oxidation

Single-ion Copper Doping Greatly Enhances Catalytic Activity of Manganese Oxides Via Electronic Interactions.

Enhancing the Low-Temperature CO Oxidation over CuO-Based -MnO<sub>2</sub> Nanowire Catalysts

Enhancing CO catalytic oxidation performance over Cu-doping manganese oxide octahedral molecular sieves catalyst

Promotional effect for SCR of NO with CO over MnO -doped Fe3O4 nanoparticles derived from metal-organic frameworks

Copper Manganese Oxides Supported on Multi-Walled Carbon Nanotubes As an Efficient Catalyst for Low Temperature CO Oxidation

Low-Temperature Catalytic Oxidation of Volatile Organic Compounds (VOCs) using Transition Metal Mixed Oxide Catalysts

The Promotion Effect of Manganese on Cu/SAPO for Selective Catalytic Reduction of NOx with NH3

Hetero-metal Cation Control of CuO Nanostructures and Their High Catalytic Performance for CO Oxidation.

Effects of different manganese precursors as promoters on catalytic performance of CuO-MnOx/TiO2 catalysts for NO removal by CO.

Preparation,Characterization and Catalytic Performance of CuO/Mn_2O_3/γ-Al_2O_3 Catalysts over CO Oxidation

One-Step Synthesis of Nanostructured Cu–Mn/TiO 2 via Flame Spray Pyrolysis: Application to Catalytic Combustion of CO and CH 4

The promotion effect of manganese on Cu/SAPO for selective catalytic reduction of NO<sub>x</sub> with NH<sub>3</sub>

Revealing the intrinsic nature of Cu- and Ce-doped Mn3O4 catalysts with positive and negative effects on CO oxidation using operando DRIFTS-MS

Manganese Doping in Cobalt Oxide Nanorods Promotes Catalytic Dehydrogenation

Surface structure effects in nanocrystal MnO2 and Ag/MnO2 catalytic oxidation of CO