Abstract:The abnormal shutdown of the pressurized water reactor (PWR) nuclear power plants can be primarily attributed to the rupturing of the heat transfer tube of the steam generator. Regardless, stress corrosion cracking is the most important ageing mechanism associated with the primary water of the PWR. In this work, the damage behavior of alloy 690 was systematically investigated using high-temperature and high-pressure in situ scratching and electrochemical techniques to understand its corrosion behavior and failure mode and provide a reference for controlling the manufacturing, processing, and installation of the alloy 690 tubing. Further, the polarization behavior of alloy 690 at different temperatures was investigated using the self-built high-temperature and high-pressure water circulation circuit system and the high-temperature and high-pressure in situ scratching device. Subsequently, the single-pass scratch in air and in situ reciprocating scratch of alloy 690 obtained using high-temperature and high-pressure water for 11 and 100 h, respectively, were studied. The samples after scratching were observed and analyzed via SEM and EDS. The results revealed the occurrence of microcracks at the bottom of the scratch during the single-pass scratch of alloy 690. The TiN inclusions with large particles were prone to fragmentation, whereas those with smaller particles were susceptible to cracking at the joint of the matrix. During the reciprocating scratch process in high-temperature and high-pressure water, a portion of the metal substrate debris at the bottom of the scratch groove was peeled off along with oxide particles, microcracks, and chipped debris. Further, the TiN inclusions with large particles were fragmented, whereas those with smaller particles easily cracked at the bonding interface of the substrate. The electrochemical signals of alloy 690 during the reciprocating scratch processes were measured using the high-temperature and high-pressure in situ electrochemical technology. The instantaneous peak current density at the scratch during the scratch process is 149 similar to 326 times of that associated with the substrate.

A New Repair Criterion for Inconel690 Alloy Steam Generator Tube with Fretting Wear

Probabilistic Structural Integrity Assessment For Inconel690 Alloy Steam Generator Tube With Volume Defect

Progress in Studying the Fretting Wear/corrosion of Nuclear Steam Generator Tubes

Crack Initiation Factor by Impact Fretting Wear at INCONEL Alloy for Steam Generator Tube in Nuclear Power Plants

High cycle fatigue behavior and numerical evaluation of Alloy 690TT steam generator tube

Microstructure and stress corrosion cracking behavior of Alloy 690TT steam generator tubes with internal bulge defect

On the role of intergranular nanocavities in long-term stress corrosion cracking of Alloy 690

Time-dependent Wear Behavior of Alloy 690 Tubes Fretted Against 405 Stainless Steel in High-Temperature Argon and Water

Comparative Analysis of Bursting Pressure Prediction Methods for Steam Generator Tube With Volume Defect

Determination of the Critical Crack Length for Steam Generator Tubing Based on Fracture-Mechanics-based Method

Fretting Corrosion-Induced Microstructural Evolution of Alloy 690TT Tube in High Temperature Pressurised Water

Environmentally Assisted Fatigue Evaluation Model of Alloy 690 Steam Generator Tube in High-Temperature Water

Fretting Wear of Alloy 690 Tube Mated with Different Materials in High Temperature Water

Weldability and Damage Evaluations of Fresh-to-Aged Reformer Furnace Tubes

Insights into stress corrosion cracking in scratched area of alloy 690TT steam generator tubes

Failure Analysis on Unexpected Fracture of the Hydraulic Expansion Mandrel for Tube to Tubesheet Expanding in the Steam Generator of Nuclear Power Plant

Investigation on the Failure Mechanistic Evolution of Fretting Corrosion of Alloy 690 with Increasing Cycles in High-Temperature Water

Effect of Contact Stress on Fretting Corrosion Behavior of Alloy 690 Tube Exposed to Simulated Secondary Water

Failure Estimation Methods for Steam Generator Tubes with Wall-Thinning or Crack

Tube-to-tube impact wear damage mechanism and nonlinear ultrasonic detection method of alloy 690 tubes

Electrochemistry and in Situ Scratch Behavior of 690 Alloy in Simulated Nuclear Power High Temperature High Pressure Water