Abstract:Combining both low-temperature activity and sintering resistance to meet practical requirements is still a great challenge for the most of effective catalysts. Herein, nano ceria with different morphologies (nanosphere, nanorod, nanocube) were applied to construct novel MnOx/CeO2 catalysts by post impregnation method for catalytic combustion of carcinogenic benzene. Detail structural/physio-chemical characterizations and activity measurements were conducted to investigate the structure-dependent behavior and interfacial effect on catalytic performance and sintering resistance properties. Compared to blank ceria supports, the low-temperature activities of all MnOx/CeO2 catalysts are significantly improved, and the T90 of best-performed MnOx/CeO2 nanorods composite is only 225 °C which is 197 °C lower than that of pure ceria nanorods. Experimental studies indicate low-temperature reducibility, oxygen mobility and surface defects could be greatly promoted by introducing hetero-interface with synergistic effects between ceria and MnOx nanocrystals. Moreover, the morphology-effect on sintering resistance is dramatically different, and the T90 of spherical MnOx/CeO2 increased to only 270 °C from 245 °C after thermal ageing at 750 °C for 100 h while this value raised to 507 °C from 256 °C on MnOx/CeO2 nanocube catalyst. This exceptional sintering resistance over spherical MnOx/CeO2 can be attributed to confinement effect of Ceria nanosphere where the supported MnOx nanoparticles is trapped in the nanopores so that it’s difficult for MnOx particles to aggregate through thermal ageing treatment. In addition, due to the small contact area between the spherical particles, there is no obvious sintering phenomenon such as growth, aggregation and collapse of the spherical particles after thermal ageing, further leading to enhancement of sintering resistance. This work provides a versatile strategy for designing highly active thermal combustion catalysts with good low-temperature activities and sintering resistance for industrial applications.

Effect of ceria morphology on the performance of MnO<sub>x</sub>/CeO<sub>2</sub> catalysts in catalytic combustion of <i>N</i>,<i>N</i>-dimethylformamide

Typical Crystal Face Effects of Different Morphology Ceria on the Activity of Pd/CeO2 Catalysts for Lean Methane Combustion

In-situ Synthesis of Monolithic Cu-Mn-Ce/cordierite Catalysts Towards VOCs Combustion

Crystal-plane effect of nanoscale CeO2 on the catalytic performance of Ni/CeO2 catalysts for methane dry reforming

Confinement effect and Hetero-interface enable High-Performing MnOx/CeO2 oxidation catalysts with exceptional sintering resistance:Morphology effect of ceria support

Crystal-plane effect of nanoscale CeO<sub>2</sub> on the catalytic performance of Ni/CeO<sub>2</sub> catalysts for methane dry reforming

Effect of the Morphology on Thermal Stability of the Ba-Ce-Mn-Al-O Oxides Synthesized in a Reverse Microemulsion

Reaction Sensitivity of Ceria Morphology Effect on Ni/CeO2 Catalysis in Propane Oxidation Reactions.

CO2 Methanation over the Ni-based Catalysts Supported on Nano-Ceo2 with Varied Morphologies

Morphology effects in MnCeOx solid solution-catalyzed NO reduction with CO: Active sites, water tolerance, and reaction pathway

Effect of MnO2 Morphology on Its Catalytic Performance in Lean Methane Combustion

Effect of Ceria Precursor on the Physicochemical and Catalytic Properties of Mn–W/CeO2 Nanocatalysts for NH3 SCR at Low Temperature

Effects of morphology and structure of titanate supports on the performance of ceria in selective catalytic reduction of NO

The effects of ceria morphology on the properties of Pd/ceria catalyst for catalytic oxidation of low-concentration methane

Catalytic Oxidation of Methane over Novel Ce?Ni?O Mixed Oxide Catalysts Prepared by Oxalate Gel-Coprecipitation

Catalytically active ceria-supported cobalt-manganese oxide nanocatalysts for oxidation of carbon monoxide.

Mn and Co decorated biomorphic ceria fiber catalysts for soot and benzene total oxidation.

CeO2 nanorod@NiPhy core‐shell catalyst for methane dry reforming: effect of simultaneous sintering prevention of CeO2 support and active Ni

Morphology and Crystal-Plane Effects of CeO2 on TiO2/CeO2 Catalysts During NH3-SCR Reaction

Effect of CeO2 morphology on performance of NiO/CeO2 catalyst in combined steam and CO2 reforming of CH4

Morphology Dependence of Catalytic Properties of Ni/CeO2 Nanostructures for Carbon Dioxide Reforming of Methane