Abstract:A series of CeO2 supports with particular morphologies (nanorods, nanocubes, nanooctas, and nanoparticles) were successfully fabricated by controlling the parameters of the hydrothermal method. The obtained nano-CeO2 materials were utilized as the supports of the Ni-based CO2 methanation catalysts prepared by the incipient impregnation method. It was found that the catalyst supported on the CeO2 nanoparticles (5Ni/NPs) exhibited much higher catalytic activity and better stability than those of catalysts with other morphological CeO2 supports. Thus, the catalytic performance of Ni/CeO2 catalysts could be facilely tuned and optimized by precisely designing the morphology of the CeO2 support. The XPS, CO2-TPD, and H2-TPR characterizing techniques showed that Ni-based catalysts supported on nano-CeO2 with varied morphologies displayed different catalytic performances. It was supposed that the typical merits, such as the abundant oxygen vacancy, medium basic sites, moderate metal-support interaction, excellent reduction ability, etc., were considered as the main origins for the enhancement of the low-temperature catalytic activities. Furthermore, the kinetic study revealed that the Ni-based catalysts supported on the nano-CeO2 with varied morphologies performed the different apparent activation energies toward CO2 methanation. The specific reaction intermediates and possible reaction pathways were carefully investigated through the in-situ DRIFTS and online TPSR techniques. Overall, this work would provide new perspectives that the roles of the morphology effect of the support ought to be emphatically considered when designing new catalysts.

Morphology Dependence of Catalytic Properties of Ni/CeO2 Nanostructures for Carbon Dioxide Reforming of Methane

Morphology-Dependent Catalytic Activity of Ru/CeO2 in Dry Reforming of Methane

Crystal-plane effect of nanoscale CeO2 on the catalytic performance of Ni/CeO2 catalysts for methane dry reforming

Morphology-Dependent Catalytic Activity of Ru/CeO<sub>2</sub> in Dry Reforming of Methane

CO2 Methanation over the Ni-based Catalysts Supported on Nano-Ceo2 with Varied Morphologies

Effect of CeO2 morphology on performance of NiO/CeO2 catalyst in combined steam and CO2 reforming of CH4

Methanol steam reforming over Ni-CeO2 model and powder catalysts: Pathways to high stability and selectivity for H2/CO2 production

Catalytic performance of Ni catalysts supported on CeO2 with different morphologies for low-temperature CO2 methanation

CO2 methanation over Ni nanoparticles inversely loaded with CeO2 and Cr2O3: Catalytic functions of metal oxide/Ni interfaces

Niobium Modification of CeO2 Tuning Electron Density of Nickel-Ceria Interfacial Sites for Enhanced CO2 Methanation

Role of CeO2 in Ni/CeO2–Al2O3 catalysts for carbon dioxide reforming of methane

Reaction Sensitivity of Ceria Morphology Effect on Ni/CeO2 Catalysis in Propane Oxidation Reactions.

Facile Route for Synthesizing Ordered Mesoporous Ni–Ce–Al Oxide Materials and Their Catalytic Performance for Methane Dry Reforming to Hydrogen and Syngas

CeO2 nanorod@NiPhy core‐shell catalyst for methane dry reforming: effect of simultaneous sintering prevention of CeO2 support and active Ni

A detailed characterization study of Ni/CeO 2 catalysts identifies Ni availability as the primary factor affecting CO 2 methanation performance

Methane Reforming with Co2 to Syngas over Ceo2-Promoted Ni/Al2o3-Zro2 Catalysts Prepared Via A Direct Sol-Gel Process

Specific Features Concerning the Mechanism of Methane Reforming by Carbon Dioxide over Ni/La2O3Catalyst

Carbon Dioxide Reforming of Methane over Cobalt‐Nickel Bimetal‐Doped Ordered Mesoporous Alumina Catalysts with Advanced Catalytic Performances

Crystal-plane effect of nanoscale CeO<sub>2</sub> on the catalytic performance of Ni/CeO<sub>2</sub> catalysts for methane dry reforming

Effects of Extrinsic Defects Originating from the Interfacial Reaction of CeO2-x-nickel Silicate on Catalytic Performance in Methane Dry Reforming

Methane reforming over Ni/Ce-ZrO2 catalysts: effect of nickel content