Room temperature multiferrocity and magnetodielectric properties of ternary (1-x) (0.94Bi_0.5Na_0.5TiO₃-0.06BaTiO₃)-xBiFeO₃ (0 ≤x≤ 0.9) solid solutions

W. J. Huang,J. Yang,Y. F. Qin,P. Xiong,D. Wang,L. H. Yin,X. W. Tang,W. H. Song,P. Tong,X. B. Zhu,Y. P. Sun

DOI: https://doi.org/10.1063/1.4986360

IF: 4

2017-01-01

Applied Physics Letters

Abstract:(1–x)(0.94Bi0.5Na0.5TiO3-0.06BaTiO3)-xBiFeO3 (0 ≤x≤ 0.9) ternary ceramics were prepared by the modified Pechini method. X ray diffraction patterns manifest that the samples undergo a gradual structural transformation from the rhombohedral-tetragonal morphotropic phase boundary to the rhombohedral phase with the increasing content of BiFeO3. Room temperature ferromagnetism was observed in BiFeO3-rich samples with x ≥ 0.6, and this ferromagnetism can be ascribed to the suppression of the spiral spin structure with the canting of antiferromagnetically ordered spins. The BiFeO3-rich samples (x = 0.6–0.8) exhibit superior ferroelectric properties with the maximum remanent polarization of 44.7 μC/cm2, as confirmed by the positive-up negative-down measurement to exclude the contribution of leakage current. The coexistence of room-temperature ferromagnetism and ferroelectricity manifests that the lead-free BiFeO3-based solid solutions are quite promising multiferroic materials and may be important for potential applications in BFO-based magnetoelectric devices.