Room Temperature Multiferrocity And Magnetodielectric Properties Of Ternary (1-X) (0.94bi(0.5)Na(0.5)Tio(3)-0.06batio(3))-Xbifeo(3) (0 <= X <= 0.9) Solid Solutions

W. J. Huang,J. Yang,Y. F. Qin,P. Xiong,D. Wang,L. H. Yin,X. W. Tang,W. H. Song,P. Tong,X. B. Zhu,Y. P. Sun

DOI: https://doi.org/10.1063/1.4986360

IF: 4

2017-01-01

Applied Physics Letters

Abstract:(1-x)(0.94Bi(0.5)Na(0.5)TiO(3)-0.06BaTiO(3))-xBiFeO(3) (0 <= x <= 0.9) ternary ceramics were prepared by the modified Pechini method. X ray diffraction patterns manifest that the samples undergo a gradual structural transformation from the rhombohedral-tetragonal morphotropic phase boundary to the rhombohedral phase with the increasing content of BiFeO3. Room temperature ferromagnetism was observed in BiFeO3-rich samples with x >= 0.6, and this ferromagnetism can be ascribed to the suppression of the spiral spin structure with the canting of antiferromagnetically ordered spins. The BiFeO3-rich samples (x = 0.6-0.8) exhibit superior ferroelectric properties with the maximum remanent polarization of 44.7 mu C/cm(2), as confirmed by the positive-up negative-down measurement to exclude the contribution of leakage current. The coexistence of room-temperature ferromagnetism and ferroelectricity manifests that the lead-free BiFeO3-based solid solutions are quite promising multiferroic materials and may be important for potential applications in BFO-based magnetoelectric devices.