Multiferroic Orders in 0.5Bifeo3–0.5bi0·5k0·5tio3

Yongxing Wei,Chenxing Bai,Weitong Zhu,Changqing Jin,Dong Gao,Gang Xu,Zengyun Jian,Yiming Zeng

DOI: https://doi.org/10.1016/j.ceramint.2019.04.249

IF: 5.532

2019-01-01

Ceramics International

Abstract:We report our studies on the multiferroic orders in 0.5BiFeO(3)-0.5Bi(0.5)K-0.5TiO3 (0.5BF-0.5BT) in this paper. The XRD pattern in the powdered form suggests a pseudocubic phase on average, with a lattice parameter of similar to 3.9572 angstrom. However, the bulk sample shows a coexistence of pseudocubic and tetragonal phases. The dielectric anomaly is relaxor-like, with the Burns temperature (T-B) of similar to 760 K. The remnant polarization (P-r, 4.02-4.25 mu C/cm(2)) is nearly unchanged in the temperature range of 298 K and 398 K. In addition, the normalized strain coefficient (d x 33) increases on heating, from 100 pm/V at 298 K up to 240 pm/V at 453 K. On the other side, two anomalies were confirmed in the temperature dependence of the magnetic susceptibilities. The high-temperature anomaly is related to a transition between the antiferromagnetic and paramagnetic states around similar to 143 K. The low-temperature anomaly around similar to 5.5 K might hint the onset of the magnetic spin glass state. We believe that some common features should be present in (Bi(x)A(1-x)) (Fe0.5B0.5)O-3 (A cations are not ferroelectric active while B cations are not magnetic active).