Abstract:(1) The simultaneously improved ferroelectric, magnetic and multiferroic properties were achieved in SrTiO3‐modified Bi0.88Sm0.12FeO3 ceramics, which can be attributed to the evolution of electronic state and the transformation of domain structure. (2) The ferroelectric domain changes from micro‐domain (x ≤ .1) to nanodomain (x ≥ .15), and the large remanent polarization was obtained at x = .1, where Pr = 49.0 μC/cm2. (3) Best magnetoelectric properties and enhanced magnetic properties were obtained at x = .1, where Mr = 59.74 emu/mol, αME = .47 mV cm–1 Oe–1. In the present study, SrTiO3 was selected to enhance the multiferroic characteristics of Bi0.88Sm0.12FeO3 (BSF) ceramics. With increasing SrTiO3 content, the principal phase of BSF ceramic transitions from rhombohedral R3c to Pna21. Through DSC and dielectric analysis, it was observed that both the Curie temperature and Néel temperature decreased proportionally with the augmentation of SrTiO3 content. When x = .1, the optimal ferroelectric performance is achieved, and the highest remanent polarization value is 55.47 μC/cm2, significantly surpassing that of BSF ceramics. Moreover, the PFM test results showed that as the substitution content increased, the domains in the BSF ceramic gradually transformed from normal ferroelectric domains to polar nanomicro‐domains. Magnetic and magnetoelectric results show that when x = .1, the best magnetic properties are obtained, Mr = 59.7 emu/mol. The magnetoelectric coefficient αME initially increased and then decreased with the increasing SrTiO3 content, reaching its optimum magnetoelectric properties at x = .1, where αME = .47 mV cm–1 Oe–1. In summary, when the substitution amount of SrTiO3 reaches 10%, the ferroelectric, magnetic, and magnetoelectric properties of BSF ceramics are significantly improved.

Significantly Enhanced Ferroelectricity and Magnetic Properties in (Sr0.5ca0.5)tio3-Modified Bifeo3 Ceramics

Effect of (Sr0.7ca0.3)tio3-Substitution on Structure, Dielectric, Ferroelectric, and Magnetic Properties of BiFeO3 Ceramics

Enhanced Ferroelectricity, Piezoelectricity and Ferromagnetism in (ba0.75ca0.25)tio3 Modified BiFeO3 Multiferroic Ceramics

Large electric‐field‐induced strain and enhanced piezoelectric constant in CuO‐modified BiFeO3‐BaTiO3 ceramics

Ferroelectric and Magnetic Properties in (1-X)bifeo3-x(0.5catio(3)-0.5smfeo(3)) Ceramics

Simultaneously Enhanced Ferroelectric and Magnetic Properties in Fe-substituted Ba4Sm2Fe Ti4-2Nb6+O30 Ceramics

Simultaneously enhanced ferroelectric and magnetic properties of SrTiO3‐modified Bi0.88Sm0.12FeO3 ceramics

Improved Structure Stability and Multiferroic Characteristics in CaTiO3‐Modified BiFeO3 Ceramics

Enhanced Multiferroic and Magnetocapacitive Properties of (1 − x)Ba0.7Ca0.3TiO3–xBiFeO3 Ceramics

Enhanced Ferroelectric Properties In Bi0.86sm0.14feo3-Based Ceramics

Simultaneously Enhanced Ferroelectric and Magnetic Properties in 0.675bife1−x Cr X O3–0.325PbTiO3 (x = 0–0.05) Ceramics

Tuning the ferroelectric transition and magnetic ordering by the polar Ba0.1Sr0.9TiO3 substitution in the multiferroic (1−x) Ba0.1Sr0.9TiO3 - xBiFeO3 (0.2 ≤ x ≤ 0.8) solid solution

Effects of Sr-substitution on Structure, Dielectric, Ferroelectric and Magnetic Properties of (Srxba1-X)4sm2fe2nb8o30 Ceramics

Room temperature multiferrocity and magnetodielectric properties of ternary (1-x) (0.94Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>-0.06BaTiO<sub>3</sub>)-xBiFeO<sub>3</sub> (0 ≤x≤ 0.9) solid solutions

Structural Evolution, Electrical Properties and Electric-Field-induced Changes of (0.8− X )pbtio 3 – X BiFeO 3 –0.2bazro 3 System Near the Morphotropic Phase Boundary

Room-temperature Multiferrocity and Magnetodielectric Properties of Ternary BiFeO3–Bi0.5Na0.5TiO3–CaTiO3 Ceramics Across the Rhombohedral–orthorhombic Phase Boundary

Multiferroic Properties of (1 −X)[0.94bi0.5na0.5tio3–0.06batio3]–xcofe2o4ceramics

Dielectric and Ferroelectric Characteristics of [(bi0.5na0.5)0.94ba0.06]1−xsrxtio3 Ceramics

Morphotropic Phase Boundary (MPB) and Enhanced Multiferroic Characteristics of Bi1-x(Ba0.75Ca0.25)xFe1-xTixO3 Ceramics (0.25≤X≤0.35)

Room Temperature Multiferrocity And Magnetodielectric Properties Of Ternary (1-X) (0.94bi(0.5)Na(0.5)Tio(3)-0.06batio(3))-Xbifeo(3) (0 <= X <= 0.9) Solid Solutions

Enhanced Multiferroic Characteristics In Nanbo3-Modified Bifeo3 Ceramics