Abstract:The work aims to extend service life and improve corrosion resistance of ink scraper. Ni-P coating and Ni-P/Al2O3 composite coating co-depositing nano Al2O3were prepared in electro-brush plating method.Corrosion behavior of Ni-P coating and Ni-P/Al2O3 composite coating in 3.5% NaCl solution by means of potentiodynamic polarization curve, corro-sion weight loss curve and AC impedance spectroscopy. Microstructure and composition of the two coatings before and after corrosion were analyzed with scanning electron microscope (SEM) and energy-dispersive spectroscope (EDS). Corrosion poten-tial of Ni-P coating, which was codeposited with nano-Al2O3, shifted positively from?0.318 V to?0.237 V, and self-corrosion current density decreased from 6.04μA to 5.75μA since standard potential of namo Al2O3was more positive than that of Ni, uniform distribution in coating led to positive shift of corrosion potential and formed corrosion microbattery with Ni-P alloy as anode and Al2O3 particle as cathode, and thereby promoted anodic polarization. After codeposition of nano Al2O3, the electro-chemical reaction resistanceRct of Ni-P/Al2O3 increased from 1.066×104?·cm2 to 2.864×104?·cm2, double-layer capacitance Cdl decreased from 43.45μF/cm2 to 27.36μF/cm2. Compared with the Ni-P coating, the surface structure of the Ni-P/Al2O3 composite coating was more compact and the defects were less. In the process of corrosion, the phosphorus and oxygen ele-ments were enriched on the surface of Ni-P coating to form a passive film which inhibited the corrosion. Codeposition of Al2O3 nanoparticles can effectively improve corrosion resistance of Ni-P coating.

ELECTRODEPOSITION AND CORROSION RESISTANCE OF Ni–W–Al<sub>2</sub>O<sub>3</sub> NANOCOMPOSITE COATINGS

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

Corrosion Behavior of Ni-P-Nano-Al2o3 Composite Coating in the Presence of Anionic and Cationic Surfactants

Composite Electroless Nickel-nano Al2O3 Coatings on Steel Substrate

Influence of Y2O3 Nanoparticles on Microstructures and Properties of Electrodeposited Ni–W–Y2O3 Nanocrystalline Coatings

Investigation on the Corrosion and Oxidation Resistance of Ni-Al2O3 Nano-Composite Coatings Prepared by Sediment Co-Deposition

Effect of Nano-Al2O3 on Corrosion Resistance of Ni-P Composite Coating by Electro-brush Plating

Investigation on Microstructure and Tribological Performances of Electrodeposited Ni-W-Y2O3 Composite Coatings

Electrodeposition, Structure and Corrosion Resistance of Nanocrystalline NiW Alloy

Preparation and Corrosion Resistance of Ni-W-CF Composite Coating on P110 Steel

Short Communication: the Corrosion Behaviors of Amorphous, Nanocrystalline and Crystalline Ni-W Alloys Coating

Deposition Mechanism and Wear Resistance Nano Ni-Al2O3 Composite Coatings

Preparation of electrochemically deposited nickel-cobalt nanocomposite coating and research on its corrosion resistance

Influence of the bath pH value on the microstructure and properties of a novel electrodeposited Ni-W-Ti3C2TX composite coating

Deposition Mechanism and Wear Resistance Nano Ni-Al<sub>2</sub>O<sub>3</sub> Composite Coatings

Microstructure evolution and improved corrosion resistance of electrodeposited NiCo-Al composite coatings with different Al contents

Sediment co-deposition of nanostructured Ni-Al2O3 composite coatings

Electroless deposition of ternary Ni–P alloy coatings containing tungsten or nano-scattered alumina composite on steel

A Study of Corrosion Resistance and Formation Characteristics of Electroless Ni–P Alloy Coatings on Al18B4O33w/6061 Al Composite with a Simple Surface Pre-Treatment

Tribological Properties and Corrosion Resistance of Porous Structure Ni-Mo/ZrO2 Alloys

Corrosion resistance of electrolessly deposited Ni–P and Ni–W–P alloys with various structures