Preparation of Novel Nano-SiO2-Gel Additive and Performance of PEM Fuel Cell

C Wang,ZQ Mao,JM Xu,XF Xie

DOI: https://doi.org/10.4028/www.scientific.net/kem.247.397

2003-01-01

Key Engineering Materials

Abstract:A novel porous nano-SiO2-gel was prepared by sol-gel technique under alkaline condition. After purified and acidified, the silica gel was provided with fine transport of protons and good permeation of gases. New type electrodes of proton exchange membrane fuel cells (PEMFCs) were fabricated with the novel silica gel additive instead of using a traditional Nafion polymer solution. The power density of PEMFC reached over 1.2 W.cm(-2), when the weight ratio of a Pt catalyst to the silica gel additive was appropriate in the catalyst layer. The silica gel was characterized by FTIR, BET and SEM, and the performance of the PEMFC was examined under polarization discharge. Experimental results indicated that the performance difference between SiO2-gel electrodes and Nafion polymer additive electrodes was not extensive. So that the lower cost and higher hydrophilicity of the silica gel could make them to be potential substitutes for perfluorosulfonic polymer additives in the catalyst layer of (PEMFCs).